The present thesis focuses on the preparation of tetragonal zirconia doped with yttria oxide, ceric dioxide, and magnesium oxide. In its theoretical part the thesis covers the characteristics of doped ceramics, the possible methods of powders preparation and of their further processing. The experimental part describes the precipitation synthesis of zirconia in base environment and further processing for ceramics. Also studied were the influences of dopant and of the processing technique used on the phase composition and microstructure of the resulting ceramics. To describe the powder structure, the thermal, dilatometric, surface area, and x-ray analyses were performed; as well as both the scanning and transmission electron microscopy employed. Dry processed ceramics showed the average grain size of 87–94 nm and the relative density in the range of 84,0–99,3 %. In comparison, the ceramics produced of hydrothermally synthesised powders proved the average grain size of 75–85 nm and the relative density between 92,7-99,9 %. As the next step, samples were subjected to low-temperature degradation for the time of 5 and 15 hours. Samples consisting of pure tetragonal ZrO2 were resistant to 5 and 15 hours of low-temperature degradation at 180 °C.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:318633 |
Date | January 2017 |
Creators | Jahodová, Daniela |
Contributors | Novotná, Lenka, Částková, Klára |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0014 seconds