This masters thesis deals with influence of cement bypass kiln dust on physico-mechanical properties of alkali activated slag and influence of chosen compounds of cement bypass kiln dust on alkali activated slag. Using alkali activated slag is limited by its shrinkage. The setting time with different amount of cement bypass kiln dust and its chosen compounds (CaO, KCl and K2SO4) were measured by isotermal and isoperibolic calorimetry too. The strength and length changes of the mixtures with different amount of cement bypass kiln dust were measured. Samples were analysed by X-Ray diffraction analysis and scanning electron microscopy. It has been found that the increasing addition of dust reduce setting time, flexural and compresive strength and shrinkage. Presence of free CaO was found being one of the reasons for accelerated setting. KCl and K2SO4 have retarding effect but influece of free CaO prevails even for its lower contents. Long-term properties evolution is strongly dependent on curing regime due to potential volume expansion.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:414115 |
| Date | January 2020 |
| Creators | Janíčková, Vlasta |
| Contributors | Kalina, Lukáš, Bílek, Vlastimil |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.002 seconds