Silicon is an ubiquitous electronic material and the discovery of strong room temperature luminescence from porous Si in 1990 raised hopes it may find a new lease of life in the emerging field of optoelectronics. First, the luminescence was shown to be emitted from nanostructures remained in a porous Si network. Later the same emission was shown from Si nanocrystals and the concept of a Si quantum dot emerged. Yet a number of different models have been proposed for the origin of light emission. Some involved interface states between a Si nanocrystal and the surrounding shell, while others considered the effect of quantum confinement in an indirect bandgap semiconductor. In this work a single Si nanocrystal was addressed to shed light on the mechanism of luminescence. Nanocrystals were prepared using e-beam lithography with subsequent etching and oxidation of silicon nanopillars. In particular, the non-uniform oxidation in self-limiting regime was successfully used to form a single nanocrystal inside nanopillars. This preparation method allowed optical probing of a single nanocrystal with far-field optics. Results revealed sharp luminescence spectra at low temperatures with a linewidth less than the corresponding thermal broadening. This property is a signature of energy level discreetness, which is, in turn, a straightforward consequence of the quantum confinement model. Another effect observed was a random on-off blinking, which is also regarded as a hallmark of single fluorescent objects. This effect appeared to be dependent on the excitation power density suggesting the involvement of Auger-assisted ionization in the dynamics of nanocrystal luminescence. In addition, it was shown how a change in the optical mode density affects the main parameters of luminescence from Si nanocrystals, such as the radiative lifetime, the quantum efficiency and the total yield. Finally, in order to clarify the influence of morphological properties, such as size or shape, of a Si quantum dot on its luminescence, combined low-temperature photoluminescence and transmission electron microscopy investigations were initiated. A method was developed using focused ion beam preparation for such a joint characterization. To conclude, the work gives support to the quantum confinement effect in explaining the light emission mechanism from nano-sized Si, as well as highlights the importance of morphological structure in the luminescence process. / QC 20100922
Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-4254 |
Date | January 2006 |
Creators | Sychugov, Ilya |
Publisher | KTH, Mikroelektronik och tillämpad fysik, MAP, Stockholm : KTH |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
Format | application/pdf |
Rights | info:eu-repo/semantics/openAccess |
Relation | Trita-ICT/MAP, ; 2007:1 |
Page generated in 0.0018 seconds