Diploma thesis deals with preparation and characterization of block copolymer PP/PE grafted with itaconic anhydride in melt. Experimental part deals with free radical iniciated grafting of polar monomers onto polyolefins and with potencial applications of grafted polyolefins. Samples of PP/PE grafted with itaconic anhydride were prepared under various conditions in the experimental part. 2,5-dimethyl-2,5bis(tert-buthylperoxy)hexane (Luperox 101) was used as radical iniciator. Grafting was performed in Brabender mixer under conditions: temperature 190-230°C, concentration of monomer 0,25-1 weight percent, concentration of iniciator 0,025 – 2 weight percent, screw speed 30 rpm. The influence of certain parameteres: iniciator concentration, monomer concentration and temperature upon conversion of monomer, value of MFI and homopolymerization of monomer extent was of interest. Presence of anhydride bonded to the polymer backbone was confirmed by FTIR spectroscopy. Concentration of grafted anhydride and conversion of monomer was determined by acid-base titration and confirmed by FTIR spectroscopy.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216542 |
| Date | January 2009 |
| Creators | Šido, Jiří |
| Contributors | Petrůj, Jaroslav, Kučera, František |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0012 seconds