The relationships between fatigue damage, stress redistribution, and residual stiffness and strength were investigated for notched graphite epoxy laminates during fulIy-reversed cyclic loads. Two material systems, AS4/3501-6 and AS4/1808, two lamination arrangements, (0,45,90,-45)<sub>s</sub>₄ and (0,45,0,-45)<sub>s</sub>₄, and two notch configurations, central hole and opposing semi-circular edge notches, were used to obtain a fundamental understanding of the fatigue effect in specimens under low and high cycle lifetimes. Damage was evaluated with penetrant-enhanced X-ray radiography and Iaminate deply. Tensile and compressive residual strengths were measured at three stages of damage development. A recently developed nondestructive testing technique, Stress Pattern Analysis by Thermal Emission, was implemented to obtain full-field measurements of surface stresses during damage initiation and growth. A new micromechanical theory of the adiabatic thermoelastic effect in Iaminated fiber composites was conceived to assist the interpretation of SPATE measurements. / Ph. D.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/53903 |
| Date | January 1988 |
| Creators | Bakis, Charles E. |
| Contributors | Engineering Physics, Henneke, Edmund G., Mook, Dean T., Plaut, Raymond H., Reifsnider, Kenneth L., Stinchcomb, W.W. |
| Publisher | Virginia Polytechnic Institute and State University |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Dissertation, Text |
| Format | xi, 200 leaves, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 18759580 |
Page generated in 0.002 seconds