In this thesis, the development of mechanical properties and structure of latex modified cementious materials during hydration was studied. Latex modified materials are composites of inorganic cement (portland cement) and organic polymer latex. Preparation, processing and fabrication of the polymer cement material based on portland cement was optimized with aim to reach the most compact structure of the product with the finest mechanical characters. The experimental part was pointed to observe influence of the type and amount of polymer latex with focus on mechanical characters and hydration kinetics with given filling as well as without it. In presented work, the possibility of compaction of the material by high-shear mixing within twin-roll mixer (the prototype for production of MDF composite) was verified. The second part of the labor was aimed to analysis of prepared polymer-cementitious material. For determination of influence of batching of added polymer latex on hydration of cement paste the thermal analysis (DTA/TGA) and infrared spectroscopy of composite was done. At last the microscopic observation by optical microscope was carried.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216351 |
| Date | January 2008 |
| Creators | Vinter, Václav |
| Contributors | Krátký, Josef, Šoukal, František |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0018 seconds