It was found that laser modified wood surfaces can be bonded together to create a wood composite without the need of any additive. This bonding method removes the need of applying adhesive, potentially lowers cost, and eliminates off gassing of petroleum resins, creating a wood product with many eco-friendly attributes. This body of work outlines a) initial chemical analysis of the laser modified surface b) its bond strength and c) the optimization of factors that control the strength of the bond.
Surface chemical analysis on laser modified wood was conducted using photo acoustic Fourier transform infrared spectroscopy (PA-FTIR) and X-Ray photoelectron spectroscopy (XPS). Light microscopy and scanning electron microscopy were utilized for surface topology analysis.Differential scanning calorimetry (DSC) quantified the thermal properties of the modified wood surface. Screening of multiple factors that would contribute to surface modification and adhesion was performed utilizing mechanical testing. Optimization of significant factors that affect bond strength was determined statistically utilizing a design of experiment approach.
Chemical analysis of the laser modified surface revealed changes in the carbonyl and aromatic regions indicating modification of the hemicellulose and lignin components, intensifying with increasing laser modification.The C1/C2 ratios found via XPS revealed that one or more of the following is occurring: more extractives have moved to the surface, condensation reactions among lignin units, and the loss of methoxy and breakage of aryl ether linkages occurred.Microscopy images showed color changes to a darker caramel color with a smoothing of surface topology, suggesting the occurrence of the softening and/or melting of wood polymers. DSC verified chemical and/or physical changes in the wood with the modified material now having a glass transition temperature between 130-150°C.DOE found that laser parameters (power and focus) as well as hot press parameters (temperature and pressure) were significant in optimizing the bond.
The impact of the study is the first documentation of the ability to laser modifies wood surfaces and subsequently bond them together. The ability of the wood polymers at the surface to undergo flow at elevated temperature is implicated in the adhesion mechanism of the laser modified wood. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/76888 |
| Date | 20 January 2011 |
| Creators | Church, William Travis |
| Contributors | Wood Science and Forest Products, Renneckar, Scott Harold, Barone, Justin R., Quesada, Henry Jose |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | en_US |
| Detected Language | English |
| Type | Thesis, Text |
| Format | application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.002 seconds