This diploma thesis deals with the development of the rheological properties of plasticized alkali-activated slag over time and depending on the timing of plasticizer and activator addition. These properties are very essential for the use of this material in practice. The main part of this work was oscillating measurements. Two types of measurements were performed – amplitude sweep and time sweep. The aim of the amplitude sweep was to determine the limit properties of the sample related to the destructive structure when the time sweep was continuous monitoring of the evolving structure. Furthermore, calorimetric measurements and solidification measurements were performed using a Vicat apparatus. The silica modulus activator and the method of adding the lignosulfonate-based plasticizer were changed for the individual mixtures. It was found that with the silica module 0 (activation with NaOH) the plasticizer works very well, better results were obtained with the addition of the plasticizer at the beginning of mixing and the activator only later. With increasing silica modulus, the importance of the presence of a plasticizer decreased.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:449702 |
| Date | January 2021 |
| Creators | Krejčová, Marie |
| Contributors | Kalina, Lukáš, Bílek, Vlastimil |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds