Li-ion batteries have become one of the chosen energy storage devices that are used in applications such as power tools, cellular phones and electric vehicles (EV). With the demand for portable high energy density devices, the rechargeable Li-ion battery has become one of the more viable energy storage systems for large scale commercial EVs because of their higher energy density to weight or volume ratio when compared to other current commercial battery energy storage systems. Various safety procedures for the use of Li-ion batteries in both consumer and EV applications have been developed by the international associations. The test procedures studied in this dissertation demonstrated the importance of determining the true capacity of a cell at various discharge rates. For this, the well known Peukert test was demonstrated. The study also showed that cells with different battery geometries and chemistries would demonstrate different thermal heating during discharge and slightly different Ragone results if different test methods were used as reported in the literature. Accelerated ageing tests were done on different cells at different Depth-of-Discharge (DoD) regions. The different DoD regions were determined according to expected stresses the electrode material in a cell would experience when discharged to specific DoD that follows the discharge voltage profile. Electrochemical Impedance Spectroscopy (EIS) was used to measure various electrochemical changes within these cells. The EIS results showed that certain observed modelled parameters would change similarly to the ageing of the cell as it aged due to the accelerated testing. EIS was also done on cells at different State-of-Charge (SoC) and temperatures. The results showed that EIS can be used as an effective technique to observe changes within a Li-ion cell as the SoC or temperature changed. For automotive vehicles that are powered by a fuel cell or battery, a supercapacitor can be coupled to a battery in order to increase and optimize the energy and power densities of the drive systems. A test procedure in the literature that evaluated the use of capacitors with Pb-acid batteries was applied to Li-ion type cells in order to quantify the increased power due to the use of a supercapacitor with a Li-ion cell. Both a cylindrical LiCoO2 cell and a VRLA Pb-acid cell showed some additional charge acceptance and delivery when connected to the supercapacitors. A LiMn2O4 pouch cell showed significant charge acceptance and delivery when connected to supercapacitors. The amount of additional charge acceptance and delivery of the different combinations could be explained by EIS, in particular, the resistance and capacitance of the cell in comparison to the combination of the cell and supercapacitor. A large capacity LiCoO2 cell showed high charge acceptance and delivery without connection with a supercapacitor. The study proved that EIS can be used to model the changes within cells under the different conditions and using different test procedures.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:nmmu/vital:10417 |
| Date | January 2012 |
| Creators | Rossouw, Claire Angela |
| Publisher | Nelson Mandela Metropolitan University, Faculty of Science |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis, Masters, MSc |
| Format | x, 228 leaves, pdf |
| Rights | Nelson Mandela Metropolitan University |
Page generated in 0.0026 seconds