We are today experiencing an increasing demand for high energy density storage devices like the lithium-ion battery for applications in portable electronic devices, electric vehicles (EV) and as interim storage for renewable energy. High capacity retention and long cycle life are prerequisites, particularly for the EV market. The key for a long cycle life is the formation of a stable solid-electrolyte interphase (SEI) layer on the surface of the negative electrode, which typically forms on the first cycles due to decomposition reactions at the electrode-electrolyte interface. More control over the surface layer can be gained when the layer is generated prior to the battery operation. Such a layer can be tailored more easily and can reduce the loss of lithium inventory considerably. In this context, water-soluble electrode binders, e.g. sodium carboxymethyl cellulose (CMC-Na) and poly(acrylic acid) (PAA), have proven themselves exceptionally useful. Since the binder is a standard component in composite electrodes anyway, its integration into the electrode fabrication process is easily accomplished. This thesis work investigates the parameters that govern binder distribution in elec-trode coatings, control the stability and electrochemical performance of the elec-trode and that determine the composition of the surface layer. Several commonly used electrode materials (graphite, silicon and lithium titanate) have been applied in order to study the impact of the binder on the electrode morphology and the differ-ent electrode-electrolyte interfaces. The results are correlated with the electrochemi-cal performance and with the SEI composition obtained by in-house and synchro-tron-based photoelectron spectroscopy (PES). The results demonstrate that the poor swellability of these water-soluble binders leads to a protection of the active material, given that the surface coverage is high and the binder evenly distributed. Although on the laboratory scale electrode formu-lations with a high binder content are common, they have little practical use in commercial devices due to the high content of inactive material. As the binder con-tent is decreased, complete surface coverage is more difficult to achieve and the binder distribution is more strongly coupled to the particle-binder interactions during the preparation process. Moreover, it is demonstrated in this thesis how these inter-actions are related to the surface area of the electrode components applied, the surface composition and the electrochemistry of the electrode. As a result of the smaller binder contents the benefits provided by CMC-Na and PAA at the electrode surface are compromised and the performance differs less distinctly from electrodes fabricated with the conventional binder, i.e. poly(vinylidene difluoride) (PVdF). Composites of alloying and conversion materials, on the other hand, typically em-ploy binders in larger amounts. Despite the frequently noted resiliency to volume expansion, which is also a positive side effect of the poor swellability of the binder in the electrolyte, the protection of the surface and the formation of a more stable interface are the major cause for the improved electrochemical behaviour, com-pared to electrodes employing PVdF binders.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:uu-317739 |
| Date | January 2017 |
| Creators | Jeschull, Fabian |
| Publisher | Uppsala universitet, Strukturkemi, Uppsala |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1651-6214 ; 1490 |
Page generated in 0.0019 seconds