Strengthening potential of single-walled carbon nanotubes (SWCNTs) in a phenolic resin composite was evaluated by characterization of purified and phenyl sulfonated SWCNTs, investigation of the load transfer capability of the purified SWCNTs, and characterization of the composites. Purified and phenyl sulfonated SWCNTs, as well as their composites, were examined by Raman spectroscopy, thermogravimetric analysis, scanning electron microscopy equipped with energy dispersive spectroscopy, transmission electron microscopy, X-ray photoelectron spectroscopy and ultra violet-visible spectrometry. Fabrication of the SWCNT/phenolic resin composite was performed by first dispersing the SWCNTs in ethylene glycol and then homogenizing the mixture with phenolic resin. The ethylene glycol was then evaporated from the mixture and the SWCNT/phenolic resin composite was cured at 200°C for 1 hour. The dispersion of SWCNTs in the phenolic resin was reduced with higher SWCNT concentrations. Load was transferred from the phenolic resin to the purified SWCNTs. This demonstrated the potential to strengthen phenolic resin composite with SWCNT reinforcement. The load transfer efficiency in total tension (0.8%) decreased with an increase in SWCNT concentration, while in total compression (-0.8%), the load transfer efficiency remained constant. At very low strain (± 0.2%), the load transfer efficiency remained constant regardless of SWCNT concentration in both tension and compression. Characterization of the phenyl sulfonated SWCNTs indicated that calcium was introduced as a contaminant that interfered with functionalization of the SWCNTs. The use of contaminated phenyl sulfonated SWCNTs resulted in macroscopic inhomogeneity within the composite.
| Identifer | oai:union.ndltd.org:ucf.edu/oai:stars.library.ucf.edu:etd-5355 |
| Date | 01 January 2010 |
| Creators | Kerr, Brittany |
| Publisher | STARS |
| Source Sets | University of Central Florida |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Electronic Theses and Dissertations |
Page generated in 0.0027 seconds