Magnetic nanoparticles have received extensive attention in the biomedical research, e.g. as prospective contrast agents for T2-weighted magnetic resonance imaging. The ability of a contrast agent to enhance the relaxation rate of 1 H in its vicinity is quantified by relaxivity. The main aim of this thesis is to evaluate the transversal re- laxivity of ε-Fe2−x Alx O3 nanoparticles coated with amorphous silica or citrate - its dependence on external magnetic field, temperature and thickness of silica coating - by means of nuclear magnetic resonance. The aluminium content x = 0.23(1) was determined from XRF, the material was further characterised by XRPD, Möss- bauer spectroscopy, DLS, TEM and magnetic measurements. The size of magnetic cores was ∼ 21 nm, the thickness of silica coating ∼ 6,10,17 and 21 nm. Magne- tization of the ε-Fe2−x Alx O3 nanoparticles increased by ∼ 30 % when compared to ε-Fe2O3. The saturating dependence of relaxivity on external magnetic field and on the linear decrease with increase of thickness of silica coating contravene the theo- retical model of motional averaging regime (MAR); nevertheless, the temperature dependence acquired in 0.47 T and 11.75 T may be explained by MAR. In compari- son to ε-Fe2O3 nanoparticles, the relaxivity of examined samples was higher for par-...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:355651 |
| Date | January 2017 |
| Creators | Kubíčková, Lenka |
| Contributors | Kohout, Jaroslav, Chlan, Vojtěch |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0134 seconds