This thesis is dedicated to the field of manufacture of heavy steel castings with resulting properties which are influenced by long solidification time. During the long solidification time a segregation process of additives in the steel occurs which results in numerous metallurgical defects. The work was intended to observe the macrosegregation effects in the wall of a heavy experimental steel casting respectively a part of a real superheavy casting intended for cement furnaces (weight 210 t). The steel casting for the research was manufactured in the joint-stock company of VHM where such heavy castings are commonly produced for the market. The supplied piece of the steel casting was cut into the smaller pieces for the better examination. The examination resulted in information about the casting macrostructure and chemical heterogeneity of chosen elements in the casting wall. The heterogeneity of the chosen elements (C, Mn, Si, Cr, S, P) is clearly shown in the worked out visual concentration maps. Based on the experimental data the measured results of segregations were confronted with the results of segregation modelling with the use of the commercial simulation software ProCAST. It resulted in the conclusion that the prediction of segregations is not in accordance with the reality. Furthermore, the results from the experimental casting are shortly compared with previously manufactured castings of the same type and the results summarizing the found range of macrosegregations of the tested sample are interpreted in the work conclusion.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:263408 |
| Date | January 2017 |
| Creators | Pernica, Vítězslav |
| Contributors | Čech, Jan, Vodárek, Vlastimil, Havlíček,, František, Šenberger, Jaroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0021 seconds