This study focuses on joining pearlitic ductile cast iron with low carbon steel by welding and investigation of this joint in microstructural and mechanical viewpoints. For this purpose E355 steel and GJS600-3 cast iron were joined using metal active gas (MAG) welding process by G3Si1 filler wire. The joining process is shaped mainly by the problems related to the low weldability of cast. Preheating was applied to prevent formation of cooling cracks and effects of post weld heat treatments (PWHT) were surveyed. Micro examination and micro hardness tests were applied to characterize the general microstructure. Grain size measurements were done for E355. Hardness profiles, tension and impact toughness properties were designated via mechanical tests. Fatigue behavior was surveyed and general fracture characteristics were determined via scanning electron microscopy (SEM) examinations.
According to study it was concluded that successful weld joint could be formed between the materials by suitable preheating. Formation of ledeburitic white cast iron and martensite in heat affected zone of cast piece was witnessed. It was possible to lower high hardness values of these phases gradually by increasing post weld heat treatment temperatures. The weld joint behaved superior to the base metals under tension and fatigue tests. In tension tests failure occurred at E355 base metal whereas fatigue loading resulted failure at GJS600-3. A great impact toughness variation was determined between two pieces. It is seen that heat treatments had minor effect on mechanical test results except hardness. The study was concluded that a useful fusion weld joint between these materials can be built.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12612992/index.pdf |
| Date | 01 March 2011 |
| Creators | Erturk, Murat Tolga |
| Contributors | Gurbuz, Riza |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0017 seconds