Aging Characteristics of an Aluminum-4.5% Copper-1.5% Magnesium Alloy

The effects of quenching conditions, single-step and two-step aging treatments on the tensile properties of an AL-4.5%Cu-1.5%Mg alloy has been investigated. Results indicate that two distinctly different precipitates of GPB and S' form during aging. Single-step aging at 140°C , 160°C and 190°C indicated that 24 hours at 160°C produced optimum strength (67 ksi UTS). Two-step aging for 3 days at 140°C plus 190°C resulted in a slight increase in strength over single step aging at 190°C. Slow (oil) quenching as well as direct quenching improved the tensile properties when aged at 190°C. Reversion occurred slowly over the temperature range 250°C to 350°C.

Identiferoai:union.ndltd.org:ucf.edu/oai:stars.library.ucf.edu:rtd-1382
Date01 January 1977
CreatorsSulouff, Robert Earl
PublisherFlorida Technological University
Source SetsUniversity of Central Florida
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
SourceRetrospective Theses and Dissertations
RightsPublic Domain

Page generated in 0.002 seconds