Two groups of magnetic oxides were investigated in this thesis. Thin films of La2/3Sr1/3MnO3 (LSMO) deposited by pulsed laser deposition (PLD) on SrTiO3 (STO) substrates were characterized by polar and longitudinal magneto-optical (MO) Kerr spectroscopy. Experimental results were compared to theoretical calculations based on the transfer matrix formalism. A very good agreement between experimental and theoretical data revealed high magnetic ordering down to 5 nm of film thickness as well as a mechanism of suppression of double exchange interaction near the LSMO/STO interface. Magnetically doped Ce1-xCoxO2-δ films deposited by PLD on MgO (x = 0.05 and 0.10) and oxidized Si (x = 0.20) substrates were studied by combination of spectroscopic ellipsometry and MO Faraday and Kerr spectroscopy. Both diagonal and off-diagonal permittivity tensor components were obtained and verified by theoretical calculations confronted with experimental data. Diagonal spectra revealed two optical transitions from oxygen to cerium states. Off-diagonal spectra revealed two paramagnetic transitions involving cobalt ions. An essential influence of cobalt doping on the resulting ferromagnetic properties of CeO2 was observed.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:341728 |
| Date | January 2014 |
| Creators | Zahradník, Martin |
| Contributors | Veis, Martin, Kouřil, Karel |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0019 seconds