Preparação e caracterização de manganitas (La,Pr)CaMnO / Preparation and characterization of La,Pr)CaMnO manganites

Amostras policristalinas de La(5/8-y)Pr(y)Ca(3/8)MnO(3); 0 y 0.625; foram produzidas pelo método da mistura estequiométrica de óxidos e tratadas termicamente ao ar a 1400 oC. As amostras foram caracterizadas através de medidas de difração de raios-X, resistividade elétrica rho(T), susceptibilidade magnética chi(T) e magnetorresistividade rho(T, H = 50 kOe). Os resultados das análises dos diagramas de raios-X indicaram que os materiais são de fase única e que houve uma substituição efetiva de La por Pr no sítio A ao longo da série. Medidas de rho(T) e chi(T) revelaram que a temperatura de transição de fase metal-isolante TMI e temperatura de Curie TC decrescem com o aumento da concentração y e que a resistividade residual rho0 (rho(T = 10 K)) é consideravelmente alta em amostras com y 0.35. Ainda, com o decréscimo de T, as amostras com y 0.35 transitam para uma fase de ordenamento de carga em TOC ~ 194 K e, em seguida, para uma fase metálica em TMI. Essas medidas também sugerem a coexistência de fases ferromagnética-metálica FMM e de ordenamento de carga isolante OCI nesses materiais. Nas propriedades físicas macroscópicas, a fase FMM mostrou ser a dominante para os compostos com pequenas concentrações de Pr (y 0.25) e a fase OCI dominante para os compostos com altas concentrações de Pr (y 0.40). As medidas de rho(T, H = 50 kOe) mostram que a magnitude da resistividade elétrica decresce drasticamente nas vizinhanças de TMI sob a aplicação de um campo magnético externo. A magnitude de MR (MR = (rho(H = 0)-rho(H = 50 kOe))/rho(H = 50 kOe)) entre os extremos da série (y = 0 e 0.625) varia até sete ordens de grandeza, sendo que o máximo valor de MR para amostras com y = 0 é de ~ 0.75 e naquelas com y = 0.625 é ~ 3.4x106 . O diagrama de fases deste composto evidencia uma região crítica (0.30 y 0.40) onde os valores de TMI, TC, MR e 0 variam abruptamente como função de y, sendo que em outras regiões tal variação é mais suave. A variação significativa desses quatro valores indica uma competição mais forte entre as fases coexistentes ocorre na região crítica. Algumas características marcantes podem ser observadas nas amostras da região crítica tais como: a presença de um segundo pico, abaixo de TMI, em ~ 90 K e ~ 72 K na curva de rho(T) de amostras com y = 0.30 e 0.35, histerese térmica mais pronunciada em rho(T) e chi(T), MR torna-se colossal, relaxação significativa da resistividade elétrica com o tempo, entre outras. Assim, as propriedades de transporte e magnéticas nessa região crítica são dominadas pela forte competição entre as fases coexistentes. / Polycrystalline samples of La(5/8-y)Pr(y)Ca(3/8)MnO(3); 0 y 0.625; were synthesized by the solid-state reaction method and sintered in air at 1400 oC. These compounds were studied by measurements of X-ray powder diffraction, magnetic susceptibility chi(T), and electrical resistivity rho(T, H). X-ray powder diffraction measurements indicated single phase materials and an effective substitution of La by Pr. Results from rho(T) and chi(T) revealed that increasing y in this series results in a rapid reduction of both the insulator to metal transition temperature TMI and the Curie temperature TC. Such a rapid decrease in TMI with increasing y is also accompanied by the occurrence of a new transition temperature, termed TCO, which is related to the transition to the charge ordered CO state. Such a temperature, which is essentially independent of y, occurs at TCO ~ 194 K and is mainly observed in samples with y 0.35. The other feature is the presence of a large residual resistivity electrical rho(0 = (10 K)) for large y (y 0.35) at low-T even though rho(T) suggests a metallic behavior below TMI. The temperature for the maximum magnetoresistance effect occurs near TMI, that shifts to higher T with increasing field. The MR is defined here as (rho(H = 0)-rho(H = 50 kOe))/rho(H = 50 kOe) and is enhanced by seven orders of magnitude from ~ 0.75 up to ~ 3.4x106 in samples with y = 0 and y = 0.625, respectively. Some features like the thermal hysteresis observed in both rho(T) and chi(T) curves indicate the coexistence of different phases in a range of y concentration, i. e., the ferromagnetic-metallic FMM and the charge ordered-insulating COI domains. The FMM is stable for y 0.25, but the COI state becomes dominant for y 0.40. There is a critical region in the phase diagram, ranging from y = 0.30 to 0.40, where the magnitude of the TMI, TC, MR, and 0 were found to display abrupt changes with increasing y. Some anomalous features like a second peak in rho(T) below TMI, a two-step increasing in chi(T), a colossal MR effect and others are observed for compositions belonging to this critical region. Our combined data suggest that the general physical properties of these compounds in such a critical region are dominated by the strong competition between coexisting ferromagnetic-metallic and charge ordered-insulating phases.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-04012011-123031
Date15 April 2005
CreatorsMasunaga, Sueli Hatsumi
ContributorsJardim, Renato de Figueiredo
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguageEnglish
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.002 seconds