Heat treatment influences structure and characteristics of treatmented material. Good heat treatment of steels for bearings ensures hardness of matrix 60 - 65 HRC, whereas structure has be formed by tempered fine needle-shaped martensite with definite part of residual austenite. Carbides should be evenly dispersed, they mustn´t create carbide network and carbide lines. Quality of steels for bearings is also influenced by volume and morphology of inclusions in the matrix. In this diploma thesis various conditions of heat treatment were to be set up with the aim of choose the optimal ones. These ensures perfect martensite transformation and full hardening of all component. Quenching from 760 °C – 770 °C was quite unsatisfactory. At this temperature resulting structure was ferritic-perlitic, because martensite transformation did not pass. Too long hold on hardening temperature also had unfavourable influence on resulting structure and characteristics. In this case, structure was created by very coarse needle-shaped martensite. Coarsening of martensite needle locally exceeded maximum allowed level. In the structure there was also possible to watch partly soluted globular carbides. Optimal heat treatment is quenching from 850 °C – 870 °C followed by tempering at 220 °C. Resulting structure quite agree with above-mentioned needs. This heat treatment can be recommended for technical practise.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:228091 |
Date | January 2008 |
Creators | Pytlíčková, Kateřina |
Contributors | Dočkal, Ing, Michael, Věchet, Stanislav |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0015 seconds