This project is in collaboration with the Hydro-Quebec Research Institute (IREQ) and the Canadian Centre for Electron Microscopy (CCEM) on the mechanical test performance of miniature-scale micro-tensile specimens. The objective of the thesis project is to create an efficient and reliable fabrication route for producing micro-tensile specimens and to validate the accuracy of a newly custom-built micro-tensile bench at IREQ. The fabrication techniques developed and outlined in this thesis use the underlying fundamental physical mechanisms of secondary electron microscopy (SEM), focused-ion beam (FIB), and the femtosecond (fs)-laser machining for producing optimal quality micro-tensile specimens.
The mechanical testing of the specimens is geared towards studying the localized deformation occurring in the microstructure when the size of the specimen only limits a number of grains and grain boundaries in order to target the specific detailed measurement of the mechanical behaviour of individual grains and interfaces. The goal for creating an optimal fabrication route for micro-tensile specimens is to carry out micro-mechanical testing of the primary turbine steels of 415 martensitic stainless steel used in the manufacture of Francis turbine components at Hydro-Quebec. The mechanical testing of single phase and interphase interface 415 steel micro-tensile specimens are considered building blocks to developing digital twin models of the steel microstructure. The experimental data from the mechanical tests would be fed into the crystal plasticity finite element models (CPFEM) that are currently being developed by researchers at IREQ. With the development of digital twin models, engineers at IREQ would be able to predict crack initiation at the microstructure level (prior to crack propagation into macro-scale cracks) by observing the evolution of the grain’s crystallographic orientation and morphology, as well as deformation mechanisms such as martensite formation and twinning produced from localized induced strains in the microstructure. In addition, self-organized dislocation processes such as dislocation nucleation and dislocation escape through the free surface can also be studied using the CPFEM models for size-limited mechanical deformation behaviour of miniature-scale mechanical test specimens.
The fabrication routes studied in this thesis project use the combination of the fs-laser and plasma focused ion beam (PFIB) to machine the micro-tensile specimens. (100) single crystal copper was the ideal material chosen to validate the accuracy of the micro-tensile bench and quality of the fs-laser-machined tensile specimens, due to its ductile nature and well-characterized properties studied in literature. A mechanical size effect was studied for single crystal copper specimens with different gauge thicknesses. It was observed from the micro-tension testing that the strength of the specimens increased with decreasing gauge thickness occurring in the size-limited tensile gauges. In addition, it was determined there was negligible differences in the size effect seen between the PFIB-machined copper micro-tensile specimens and the fs-laser-machined micro-tensile specimens, demonstrating that the fs-laser is a reliable machining route for the micro-tensile specimens.
X-ray computed tomography was used to validate the correct geometry of the machined gauge section produced from an innovative gauge thinning method adopted from IREQ’s research collaborator, Dr. Robert Wheeler. As well, finite-element analysis (FEA) was performed to determine the deformation behaviour under both linear-elastic and non-linear elastoplastic conditions of (100) copper and 415 steel models simulated in pure tension, prior to the fabrication of the micro-tensile specimens, respectively.
Furthermore, significant progress has been made towards targeting martensite grains in the 415-steel microstructure using electron backscattered diffraction (EBSD) analysis to produce single crystal and interphase interface micro-tensile specimens. A workflow towards grain targeting using EBSD analysis has been developed, as well as for the relocation of grains using reference fiducial marks for future fabrication of the single crystal and interphase interface 415 micro-tensile specimens. / Thesis / Master of Applied Science (MASc) / Hydro-Quebec is an energy utilities company that operates the design of Francis hydro-turbines to supply hydroelectric power across the province of Quebec. The hydro-turbines have an expected service life of 70 years. Unfortunately, the turbines can get replaced by new ones prior to reaching half of its service life, due to the development of severe fatigue crack growth in the primary components of the turbines. A solution proposed by the researchers at the Hydro-Quebec Research Institute (IREQ) is to determine a linkage between the turbine’s steel’s microstructure and the mechanical behaviour of the turbine steels. Deformation of the material starts at the microstructure level, where dislocations glide through the material lattice, causing both reversible (elastic) and irreversible (plastic) deformation. Therefore, a solution was proposed by the researchers at IREQ to create computational models of the steel microstructure to predict the deformation of the steel’s microstructure. Being able to predict the deformation mechanisms through the simulation models of the microstructures allows for engineers at Hydro-Quebec to schedule regular maintenance of the turbines more efficiently and provide metallurgists the knowledge on what is occurring at the microstructure level and what can be done to improve the chemical and physical composition of the steel. To develop the digital twin models, experimental data must be collected through mechanical testing of miniature mechanical test specimens of the turbine steels. The mechanical properties of the single phases and interphase interface specimens are fed into the models as building blocks to building a microstructure map of the turbine steels. Micro-tension testing of micro-tensile specimen provides direct information about the material’s mechanical properties. In this work, a reliable and efficient fabrication route for micro-tensile specimens was developed for the purpose of extracting mechanical properties of single phase and interphase interface turbine steel specimens using focused ion beam (FIB) and femtosecond laser machining.
| Identifer | oai:union.ndltd.org:mcmaster.ca/oai:macsphere.mcmaster.ca:11375/29112 |
| Date | January 2023 |
| Creators | Huang, Betty |
| Contributors | Basim, Nabil, Materials Science and Engineering |
| Source Sets | McMaster University |
| Language | English |
| Detected Language | English |
| Type | Thesis |
Page generated in 0.0103 seconds