2009_SuelenVanessaMirandadasChagas.pdf: 3931690 bytes, checksum: b31799f0634da12b4ef26217edc0a197 (MD5) / Nos últimos anos, observa-se um aumento na incidência de descolamento de placas cerâmicas nas fachadas das edificações. Isto se deve a inúmeros fatores, dentre os quais destaca-se a variação de temperatura que provoca solicitações cíclicas nas fachadas, sobretudo na interface argamassa de emboço/argamassa colante/cerâmica, até a sua ruptura por fadiga. Nesse sentido, sabendo-se que o emboço constitui o “corpo do revestimento” que serve de suporte para as outras camadas, o objetivo desta pesquisa é estudar o comportamento das argamassas de revestimento do emboço submetidas a carregamentos cíclicos de compressão. Para isto, inicialmente, foram realizados ensaios de caracterização das argamassas industrializadas e argamassas mistas, sendo em seguida proposta uma metodologia de ensaio de fadiga sob compressão para as mesmas. Com os resultados obtidos nos ensaios de compressão estática, é possível definir os níveis de tensão empregados no ensaio de fadiga. A partir do número de ciclos necessários para a ruptura, é traçada a curva “S-N” (tensão alternada versus número de ciclos) das argamassas de emboço sujeita à fadiga sob compressão. Observa-se que o limite de resistência à fadiga sob compressão especificamente das argamassas empregada nos ensaios é de 7,53Mpa para a argamassa industrializada, enquanto que para a argamassa mista o valor encontrado é de 6,26MPa. Tais valores correspondem a aproximadamente 73% da tensão de ruptura estática da argamassa industrializada e da argamassa mista, respectivamente. Finalmente, para avaliar a resistência à fadiga é adotada a curva de ruptura de Coulomb-Mohr no estado plano e no estado tridimensional, as quais são traçadas com os valores das resistências de fadiga para 1 ciclo e para 106 ciclos de carregamento, nas quais é possível definir uma região em que não há preocupação com a ruptura sob fadiga. ________________________________________________________________________________ ABSTRACT / In recent years, there is an increased incidence of detachment of tiles on the buildings facades. This is due to several factors, among which we highlight the temperature variation that causes cyclical stress on the facades, especially at the interface of rendering / dry-set mortar / ceramic, provoking its fatigue failure. In this sense, given that the rendering is "it coating body" that serves as support for other layers, the objective this research is study the behavior of mortar coating subjected to cyclic compressive loads. For this, initially, the characterization of industrial mortars and mixed mortar were conducted and then a methodology for fatigue test under compression for the same has been proposed. With the results obtained in test static compression, is can set the stress levels used in the fatigue test. The “S-N” curve (alternating stress vs. number of cycles) for mortar subject to fatigue under compression is obtained from the number of cycles required to rupture. Observe that the limit of fatigue resistance of the mortar under compression specifically mortars used in the tests is 7.53 MPa for industrial mortar, while the mixed mortar the value found is 6.26 MPa. These values correspond to approximately 73% of static resistance of industrialized mortar and mixed mortar, respectively. Finally, to evaluate the fatigue resistance of mortars is adopted the curve Coulomb-Mohr in the state plan and state three-dimensional, which are drawn with the values of fatigue resistance for 1 cycle and 106 cycles of loading, where is can define a region where there is not concern about the under fatigue rupture.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unb.br:10482/7601 |
| Date | 30 November 2009 |
| Creators | Chagas, Suelen Vanessa Miranda das |
| Contributors | Bezerra, Luciano Mendes, Bauer, Elton |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UnB, instname:Universidade de Brasília, instacron:UNB |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0024 seconds