000822661.pdf: 3005956 bytes, checksum: aa617124450c9641b6ecb66c3cbbdaa9 (MD5) / Comparou-se a resistência de união (RU) dos cimentos resinosos Panavia F (P) (Kuraray) e RelyX U200 (R) (3M ESPE) à cerâmica zircônia através de três diferentes métodos de tratamento da superfície: 1- silicatização triboquímica (ST) (Rocatec Soft - 3M ESPE); 2- glaze (G) (Akyzent glaze spray- VITA); 3- aplicação de vidro bioativo (VBA). Blocos pré-sinterizados do sistema Zirkonzahn (Zirkonzahn) foram seccionados de modo a produzir 90 blocos menores (5 x 4 x 3 mm). Os blocos foram polidos em Politriz com lixas d’água de granulação fina 1000 e 1200 (3M ESPE) e limpos em banho ultrassônico contendo álcool isopropílico a 96% durante 5 min. Após a sinterização dos blocos cerâmicos, foi realizada a aplicação do tratamento de superfície. O Rocatec Soft foi jateado com 2,8 bar, ângulo de incidência perpendicular e distância padrão de 10 mm por 25 s em movimentos circulares. O Akyzent Glaze Spray foi pulverizado por 2 s e em seguida sinterizado em forno Vacumat (Vita) de acordo com recomendações do fabricante. Após a aplicação de 1 gota do vidro bioativo, procedeu-se a secagem e sinterização a 1200 ºC deste material. Em todos os grupos aplicou-se agente de união silano Monobond-S (Ivoclar Vivadent). Nos grupos 3, 4, 5 e 6 a superfície foi primeiramente condicionada com ácido hidrofluorídrico (HF) a 5% durante 2 min, lavada e depois silanizada. A cimentação foi realizada com um dispositivo (Ultradent), produzindo cilindros de cimento resinoso com 2 x 1mm.! Após 24 h os espécimes foram envelhecidos em termocicladora com 5.000 ciclos com banhos de temperatura entre 5 e 55 ºC e submetidos ao ensaio de cisalhamento na Shear Bond Tester (Bisco). O VBA foi analisado qualitativamente por meio de análise térmica diferencial (DTA), através de difração de raios-x (DRX)(Panalytical) e espectroscopia de energia dispersiva de raio-x (EDS) (Oxford Instruments)... / The bond strength of resin cements Panavia F (P) (Kuraray) and RelyX U200 (R) (3M ESPE) to zirconia using three different surface treatments: 1 - triboquemical silicatization (ST); 2 - glaze (G) 3 - bioactive glass (VBA) was compared. Blocks of Zirkonzahn system were cut producing 90 smaller blocks (5 x 4 x 3 mm). The blocks were polished with water finegrained 1000 and 1200 sandpaper in Politriz and cleaned with 96% isopropyl alcohol for 5 min. The Rocatec Soft was etched with 2.8 bar, in a perpendicular way and a distance of 10 mm for 25 s in a circular motion. The Akyzent Glaze Spray was sprayed by 2s and then sintered in oven Vacumat (Vita) according to manufacturer's recommendations. After application of 1 drop of bioactive glass, the material was dried and sintered at 1200 °C. In all groups was applied silane coupling agent Monobond- S (Ivoclar Vivadent). In groups 3, 4, 5 and 6 the surface was first etched with 5% hydrofluoric acid (HF) and then silanized. The cementing was carried out with a device (Ultradent), producing cured cement cylinders of 2 x 1mm. After 24 h the specimens were aged in thermocycler with 5,000 cycles at a temperature of 5 and 55 ºC and subjected to microshear test on Shear Bond Tester (Bisco). VBA was analyzed by means of DTA, XRD and EDS. Optical profilometry (PO) was performed to obtain roughness. After fracture the samples were analyzed through SEM. It was found that XRD revealed the formation of a glass ceramic film. DTA shows that the temperature of 1200 °C is the most suitable for sintering. DRX showed the formation of a glass ceramic film. According to ANOVA, the interaction effect was significant (p = 0.003 < 0.05). The test for multiple comparison of means, Tukey (5%) showed that the TBS (MPa) for VBA were significantly higher than the other groups (with 26.94 ± 3.50 to P and 28.36 ± 3.32 to R), regardless cement kind used. The lowest result...
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/123259 |
| Date | 08 April 2014 |
| Creators | Antunes, Débora Pinto [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Pagani, Clovis [UNESP], Santos Júnior, Gildo Coelho [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 100 f. : il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1, -1 |
Page generated in 0.0143 seconds