Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-18T10:00:07Z (GMT). No. of bitstreams: 1
Henriques_GuilhermeEliasPessanha_M.pdf: 3082477 bytes, checksum: 9387401241e8fa339536480dc617cfc9 (MD5)
Previous issue date: 1993 / Resumo: O objetivo deste trabalho foi avaliar a resistência flexural das ligas do sistema Co-Cr Dentorium, Duracrom e Steeldent, disponíveis comercialmente, submetendo-as ou não à soldagem, utilizando amostras confeccionadas com liga nova exclusivamente ou mistura de proporções iguais de ligas nova e previamente fundida. Foram confeccionadas vinte amostras com formato em halteres, para cada uma das ligas avaliadas, divididas em quatro grupos, seguindo o critério a seguir: liga nova sem solda; liga nova/refundida sem solda; liga nova com solda; e, liga nova/refundida com solda. As amostras foram fundidas mediante a utilização de fonte elétrica de arco voltaico de carbono e para o procedimento de soldagem, foi utilizada liga para solda de alta temperatura à base de Co-Cr, fundida sob chama redutora de maçarico de oxiacetileno, estando as partes a serem unidas, distantes 0,4 mm entre si. Para a avaliação da resistência flexural, as amostras foram submetidas à carga perpendicular de compressão fornecida por máquina de teste universal, com velocidade de 200 Kgf /min. Posteriormente, a superfície de fratura das amostras, foi analisada sob microscopia eletrônica de varredura. Com base nos resultados obtidos, verificamos que: a) as ligas Dentorium e Steeldent, tanto na condição de nova, quanto na condição de misturadas, não mostraram diferenças estatisticamente significativas em termos de resistência flexural; b) a liga Duracrom registrou redução nos valores de resistência flexural quando misturada com ligas nova e refundida; c) para as três ligas avaliadas, tanto na condição de nova como na condição de misturadas, houve redução nos valores de resistência flexural para aproximadamente 1/4 daqueles obtidos com as amostras livres de solda / Abstract: The purpose of this investigation was to determine the flexural strength of Dentorium, Duracrom and Steeldent, commercially available Co-Cr based alloys, subdued or not to soldering procedure, using only new alloy or a mixture of new and previously casted alloy. Twenty dumb-shaped specimens were manufactured for each one of the alloys, divided into four groups as the following rule: new alloy without soldering procedure; new alloy/casted alloy combination without soldering procedure; new alloy with soldering procedure; and, new alloy/casted alloy combination with soldering procedure. The specimens were cast with carbon voltaic arc as the electric heat source and for the soldering procedure, it was used high-temperature Co-Cr solder alloy, melted with the reducing flame of a oxyacetilene torch as the heat source, while the gap distance was maintained at 0.4 mm. To evaluate the flexural strength, the specimens were submited to perpendicular compression stress provided by the universal testing machine, with a c:ross-head speed of 200 Kgf/min. After that, the fracture surfaces were observed under scanhing electron microscopy. Related to the results, it was verified that: a) Dentorium and Steeldent alloys, neither as one-half new nor as a half-new/once-used combination, showed no statistically significant differences; b) Duracrom alloy showed reduced flexural strength values when conducted in the as mixed condition; c:) either as new or as mixed, the soldered three alloys displayed reduction of about 1/4 in the flexural strength values, when compared with those obtained with the non soldered ones / Mestrado / Materiais Dentarios / Mestre em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290074 |
| Date | 18 July 2018 |
| Creators | Henriques, Guilherme Elias Pessanha, 1968- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Consani, Simonides, 1939- |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 100f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0022 seconds