In this investigation, polymer precursor of syntactic foam has been reinforced with SiC nanoparticles to enhance mechanical and fracture properties. Derakane 8084 vinyl ester resin was first dispersed with 1.0 wt% of SiC particles using a sonic cavitation technique. In the next step, 30.0 wt% of microspheres (3M hollow glass borosilicate, S-series) were mechanically mixed with the nanophased vinyl ester resin, and cast into rectangular molds. A small amount of styrene was used as dilutant to facilitate mixing of microspheres. The size of microspheres and SiC nanoparticles were 20-30 um and 30-50 nm, respectively. Tension, compression, and flexure tests were conducted following ASTM standards and a consistent improvement in strength and modulus within 20-35% range was observed. Fracture toughness parameters such as KIC and GIC were also determined using ASTM E-399. An improvement of about 11-15% was observed. Samples were also subjected to various environmental conditions and degradation in material properties is reported. / by Debdutta Das. / Thesis (M.S.C.S.)--Florida Atlantic University, 2009. / Includes bibliography. / Electronic reproduction. Boca Raton, Fla., 2009. Mode of access: World Wide Web.
| Identifer | oai:union.ndltd.org:fau.edu/oai:fau.digital.flvc.org:fau_4234 |
| Date | January 1900 |
| Contributors | Das, Debdutta., College of Engineering and Computer Science, Department of Ocean and Mechanical Engineering |
| Publisher | Florida Atlantic University |
| Source Sets | Florida Atlantic University |
| Language | English |
| Detected Language | English |
| Type | Text, Electronic Thesis or Dissertation |
| Format | xii, 65 p. : ill. (some col.), electronic |
| Rights | http://rightsstatements.org/vocab/InC/1.0/ |
Page generated in 0.0016 seconds