Previous issue date: 2017-02-20 / Capes / Biodiesel, que é produzido a partir de óleos vegetais ou gorduras animais através da reação de transesterificação com álcool é um excelente substituto para o diesel de petróleo por ser um combustível biodegradável derivado de fontes renováveis. A peneira molecular MCM-41 apresenta potencial para processamento de ácidos graxos visando a produção de biodiesel, por controle da composição química e por tratamentos químicos posterior a sua síntese. A inserção de óxidos metálicos pode proporcionar um aumento no desempenho catalítico da peneira molecular, possibilitando a preparação de catalisadores com maior atividade, seletividade e estabilidade térmica. O presente trabalho tem como objetivo principal a obtenção de biodiesel a partir da reação de transesterificação do óleo de soja utilizando o catalisador MoO3/25CeO2/MCM-41. Para tal afinidade, a peneira molecular foi preparada partindo-se de um gel com a seguinte composição molar da mistura reacional: 1SiO2 : 0,30 CTABr : 11 NH3 : 144 H2O. A incorporação do cério e molibdênio (em peso) no suporte MCM-41 foi por via seca. Através dos difratogramas foi possível identificar os picos característicos da peneira molecular MCM-41, como também as fases dos óxidos de cério e molibdênio na estrutura da peneira molecular, confirmando os processos de impregnação. Por meio da isoterma de adsorção de nitrogênio a peneira molecular apresentou uma área superficial SBET de 1072 m2/g e isoterma do tipo IV característica de materiais mesoporosos. O catalisador contendo 15% em peso de molibdênio e 25% em peso de cério atingiu a maior conversão em éster metílico em torno de 93% como também densidade de 0.8832 g/cm3, viscosidade cinemática 4,044 mm2/s e acidez de 0,49 mg KOH/g. / Biodiesel, which is produced from vegetable oils or animal fats by transesterification
reaction with alcohol, is an excellent substitute for diesel oil being a biodegradable fuel
derived from renewable. The molecular sieve MCM-41 has the potential to process fatty
acids aiming biodiesel production, by controlling the chemical composition and
subsequent chemical treatments to their synthesis. The inclusion of metallic oxides can
provide an increase in catalytic performance of the molecular sieve, allowing th e
preparation of catalysts with higher activity, selectivity and thermal stability. This study
aims to obtain biodiesel from the transesterification reaction of soybean oil using the catalyst MoO3/25CeO2/MCM-41. To this affinity, the molecular sieve was prepared
starting with a gel with the following molar composition of the reaction mixture: 1SiO2
: 0,30 CTABr : 11 NH3 : 144 H2O. The incorporation of cerium and molybdenum (by
weight) in the MCM-41 was supported by dry. Through the XRD patterns it was
possible to identify the peaks characteristic of MCM-41 molecular sieve, as well as
phases of cerium and molybdenum oxides in the molecular sieve structure, confirming
the impregnation process. By means of the nitrogen adsorption isotherm molecular
sieve had a surface area SBET de 1072 m2/g and isotherm type IV characteristic of mesoporous materials. The catalyst containing 15% by weight molybdenum and 25%
by weight cerium reached the highest methyl ester conversion around 93% as well as
density of 0.8832 g/cm3, kinematic viscosity 4,044 mm2/s and acidity of 0,49 mg
KOH/g
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/1544 |
Date | 23 August 2018 |
Creators | BARROS, Thiago Rodrigo Barbosa. |
Contributors | SOUSA, Bianca Viana de., ARAÚJO, Antônio Carlos Brandão de., ALVES, José Jailson Nicacio., ALMEIDA, Marcello Maia de. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0017 seconds