Comportamento de desgaste de pares Metal-Compósito de grau aeronáutico / Wear behavior of aeronautical grade metal / composite pairs

Estudou-se o comportamento de desgaste sob deslizamento em múltiplos passes de pinos fixos de liga metálica friccionados contra discos rotativos de laminados compósitos de matriz polimérica fortalecidos com fibras contínuas de carbono (C), para distintas cargas aplicadas e temperaturas de ensaio. Determinou-se a perda de volume por desgaste dos diversos pares tribológicos, e avaliaram-se os principais aspectos das superfícies e dos produtos gerados durante o processo de desgaste. Concluiu-se que o par formado pelo aço inoxidável martensítico PH 15-5 e o laminado compósito termoplástico C-PPS (poli-sulfeto de fenileno) apresentou o menor desgaste na maioria das circunstâncias avaliadas. A liga Ti6Al4V foi a pior opção dentre os pinos metálicos, independentemente do laminado compósito empregado, devido à baixa resistência ao cisalhamento e alta rugosidade superficial do metal, a qual prejudicou o ancoramento de filmes poliméricos de transferência. O ótimo desempenho do aço PH resultou de sua alta dureza e da adequada rugosidade superficial para o efetivo ancoramento do filme de transferência. O laminado compósito C-PPS se mostrou mais susceptível às variações na carga de contato, enquanto que o C-EPX (Epóxi) foi mais sensível à temperatura de ensaio. Filmes poliméricos de transferência atuaram como lubrificante do sistema tribológico, preservando ambos o pino metálico e o disco compósito de um desgaste excessivo. A natureza dos produtos de desgaste, sua geometria, seu tamanho médio e sua distribuição de tamanhos dependeram fortemente do disco rotativo de laminado compósito e das condições de ensaio de desgaste, e afetaram sobremaneira, como terceiro corpo abrasivo, o subseqüente processo de desgaste dos pares de fricção metal-compósito. Os resultados obtidos são potencialmente úteis na especificação de juntas mecânicas aeronáuticas mais apropriadas de laminados compósitos de matriz polimérica unidos por intermédio de prendedores metálicos. / Multipass sliding wear behavior of static metal alloy pins rubbing against rotating carbon fiber reinforcing polymer matrix composite laminate disks has been studied for different applied loads and test temperatures. The volume loss due wear has been determined for several tribological metal / composite systems, and the main aspects of wear surfaces and debris have been evaluated. It has been concluded that the best performance was achieved in very most cases by the PH15-5 steel pin contacting the C-PPS (poly-phenylene sulphide) disk. The Ti6Al4V alloy displayed the worst performance among the metal pins, regardless the employed composite laminate, as a result of the metal´s low shear strength and high surface roughness, which impaired the formation of polymer transfer films. The outstanding performance of PH steel pins derived from its high hardness and proper surface roughness that favored the transfer film formation. The C-PPS composite laminate was more sensitive to contact load variations, whereas the C-EPX laminate was more susceptible to the test temperature. Polymer transfer films acted as lubricant in the tribological system, preserving both the metallic pin and the composite disk from wearing in excess. The nature of wear debris, their geometry, mean size, and size distribution strongly depended on the composite laminate disk as well as on testing conditions, and affected overwhelmingly, as third body abrasive particles, the subsequent wear process of metal / composite friction pairs. The obtained results are potentially useful for the specification of more equalized aircraft mechanical joints comprising polymer matrix composite laminates and metallic fasteners.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-16092009-145305
Date08 June 2009
CreatorsFreitas, Amilton Joaquim Cordeiro de
ContributorsTarpani, José Ricardo
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeDissertação de Mestrado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.002 seconds