Non-metallic inclusions (NMI) are small impurities that can always be found in steel and other materials. NMIs are of great importance because they may negatively impact various properties of the steel, depending on their composition, morphology and numbers. In the oil and gas industry, one of the most concerning property that can be affected by the NMIs is corrosion resistance. In this report, certain aspects of NMIs were investigated, such as size or composition and effect which they have on the corrosion resistance. To accomplish this, two different steel alloy samples from pipelines were analyzed using electrolytic extraction,a scanning electron microscope (SEM) and a software called ImageJ. The results showed that only Niobium-Titanium carbides (NbTi-C) which were found on one of the samples had the potential to be dangerous, due to them causing pits ranging from 1 to 12.5 times their inclusion size. It was also found out that the size of the inclusions did not affect the size of the pitting that they caused. / Icke metalliska inneslutningar (NMI) är små föroreningar som alltid finns i stål och andramaterial. NMI:er är mycket viktiga eftersom de kan negativt påverka olika egenskaper hos stål, beroende på deras komposition, morfologi och antal. I olje -och gasindustrin är en särskilt oroande egenskap som kan påverkas av NMI:er deras korrosionsmotstånd. I denna rapport undersöktes hur olika aspekter hos NMI:er, som storlek eller komposition, påverkade korrosionsmotståndet i rostfritt stål. För att utföra detta analyserades två olika stållegeringsprovbitar från pipelines med elektrolytisk extraktion, ett svepelektronmikroskop (SEM) och ett program som kallas ImageJ. Från resultatet framkom det att baraNiob-Titankarbider (NbTi-C) som fanns på en av provbitarna hade potentialen att vara farlig, då den orsakar gropar som är 1 till 12.5 gånger större än sin egen storlek. Det framkom också att storleken på inneslutningarna inte påverkade storleken på deras gropar.
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-277900 |
| Date | January 2020 |
| Creators | Brisenmark, Emil, Jönsson Valencik, Jane |
| Publisher | KTH, Materialvetenskap |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | TRITA-ITM-EX ; 2020:313 |
Page generated in 0.0017 seconds