Segregation which occurs in slowly cooled castings and in the direction indicated by the equilibrium diagram is called "normal segregation". The first crystals to separate from the molten alloy during solidification are rich in the higher melting point alloy and occupy a position close to the mold face. As the solidification proceeds the growing dendrites push before them the residual liquid which is becoming continually enriched in the lower melting point alloy (usually the alloy of high solute concentration). [...]
Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:QMM.111113 |
Date | January 1956 |
Creators | Youdelis, William V. |
Contributors | Kirkaldy, J.S. (Supervisor) |
Publisher | McGill University |
Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
Language | English |
Detected Language | English |
Type | Electronic Thesis or Dissertation |
Format | application/pdf |
Coverage | Master of Engineering. (Department of Metallurgical Engineering.) |
Rights | All items in eScholarship@McGill are protected by copyright with all rights reserved unless otherwise indicated. |
Relation | alephsysno: NNNNNNNNN, Theses scanned by McGill Library. |
Page generated in 0.0074 seconds