Sol-gel (solution-gelation) method was used to prepare Ni-Ti and Ni-Ti-Al catalysts for reforming of methane with carbon dioxide. This method, after optimizing the parameters such as hydrolysis and acid/alkoxide ratio, is able to make a Ni-Ti catalyst with a surface area as high as 426m2/g when calcined at 473K; but calcination at higher temperature lead to dramatic decrease in surface area. XRD, XPS, TEM and SEM were used to understand this change.
Using a packed bed reactor, the catalysts were evaluated with the reforming reaction. It was found that the activity of the Ni-Ti catalyst increases with the Ni loading in the range of 1-10wt%. The reduction temperature has strong effect on activity of the reduced catalyst. Up to 973K, the activity increases with the reduction temperature; but after 973K, the activity decreases and become 0 when the temperature is over 1023K. The Ni-Ti catalyst also deactivated as 15% after 4h of time on stream. The XRD analysis shows that Ti3O5 formed in the catalyst after higher-temperature reduction as well as after the reaction for a period of time. The formation of Ti3O5 may render the catalyst to loss its activity. However, further study is expected to understand the mechanism. TG/DTA analysis shows that both Ni-Ti and Ni-Ti-Al catalysts had carbon deposition; but the latter maintained higher activity in a longer period of time.
| Identifer | oai:union.ndltd.org:USASK/oai:usask.ca:etd-08042005-163530 |
| Date | 07 August 2005 |
| Creators | Sun, Haijun |
| Contributors | Wang, Hui, Pugsley, Todd, Foley, Stephen R., Dalai, Ajay K. |
| Publisher | University of Saskatchewan |
| Source Sets | University of Saskatchewan Library |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://library.usask.ca/theses/available/etd-08042005-163530/ |
| Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0013 seconds