Orientador: Brenda Paula Figueiredo de Almeida Gomes / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:24:46Z (GMT). No. of bitstreams: 1
Sena_NeyllaTeixeira_D.pdf: 3038730 bytes, checksum: 1cacde1c32eceda5813f7908699bd2f9 (MD5)
Previous issue date: 2009 / Resumo: Este estudo investigou: a) a atividade antimicrobiana de cimentos endodônticos (AH Plus e Epiphany) frente a microrganismos encontrados na microbiota intracanal (Enterococcus faecalis, Staphylococcus aureus, Actinomyces naeslundii e Candida albicans); b) a microinfiltração coronária de dentes obturados com AH Plus/ guta-percha e Epiphany/ Resilon; c) os possíveis efeitos antimicrobianos residuais destas substâncias nos cones quando em contato com E. faecalis e Porphyromonas gingivalis, d) as alterações na superfície dos cones de guta-percha e Resilon expostos à desinfecção com clorexidina gel 2% e hipoclorito de sódio 5,25%. A ação antimicrobiana dos cimentos foi testada através de dois métodos: o de contato direto nos tempos: imediato, 24 h, 48 h, 7 e 14 dias após a espatulação, e através do teste de difusão em Agar. A avaliação da microinfiltração coronária de dentes obturados endodonticamente foi acompanhada diariamente por 90 dias após a contaminação. A ação residual dos agentes desinfetantes sobre a superfície dos cones foi observada através do método de difusão em Agar (nos períodos de 1, 5, 10, 20 e 30 min), e as alterações estruturais na superfície dos cones foram testadas através de análise em Microscópio Eletrônico de Varredura (MEV). Quanto ao método de contato direto os resultados foram: O cimento AH Plus teve maior atividade antimicrobiana que o Epiphany, o Epiphany apresentou grande dissolução em todos os tempos testados (p<0.05), A. naeslundii foi o microrganismo mais suscetível e E. faecalis o mais resistente a todos os cimentos testados. Quanto ao método de difusão em Agar a maior atividade antimicrobiana foi a do Primer, seguida do AH Plus e do Epiphany. C. albicans foi o microrganismo mais suscetível e o S. aureus o mais resistente. Quanto à prevenção da microinfiltração coronária, AH Plus/guta-percha foi superior ao sistema Epiphany (p<0.05). Os dentes obturados com o sistema Epiphany apresentaram clinicamente alterações de cor em suas raízes. Quanto à atividade antimicrobiana das substâncias químicas auxiliares sobre os cones, estas foram incapazes de se unirem aos componentes dos cones de guta-percha e de apresentarem efeito residual. Entretanto o cone de Resilon apresentou ação antibacteriana residual quando exposto a clorexidina gel. Quanto às alterações estruturais dos cones em MEV, não foi encontrada modificação nas características superficiais dos cones e nem presença de cristais de cloreto. Em conclusão, os resultados sugerem que o sistema Epiphany não demonstrou ser superior ao AH Plus quanto à ação antimicrobiana e à prevenção da microinfiltração coronária, e que as substâncias químicas auxiliares usadas na desinfecção dos cones de guta-percha e de Resilon não apresentaram ação residual nos cones de guta-percha e nem alteraram a superfície dos dois tipos de cones testados. Entretanto o cone de Resilon apresentou ação antibacteriana residual quando exposto à clorexidina gel. / Abstract: The aims of the present study were to investigate: a) the antimicrobial property of endodontic sealers (AH Plus and Epiphany) against the following microorganisms: Enterococcus faecalis, Staphylococcus aureus, Actinomyces naeslundii and Candida albicans; b) the coronal microleakage of teeth obturated with AH Plus/ gutta-percha and Epiphany/ Resilon; c) to evaluate the alterations on the surface of the gutta-percha and Resilon cones disinfected with 2% CHX-gel and 5.25% NaOCl; d) the possible residual antimicrobial properties of these substances on the cones when in contact with E. faecalis and Porphyromonas gingivalis. The antimicrobial properties of endodontic sealers were tested by two methods: the direct contact at different times (immediately, 24/ 48 hours and after 7/14 days) and the Agar diffusion method. The coronal microleakage was followed daily during 90 days after contamination. The residual property of the disinfectant agents on the cones was tested by the Agar diffusion method (at 1, 5, 10, 20 and 30 min) and the alterations on the surface structure of the cones were observed by the Scanning Electron Microscopy (SEM) analysis. Regarding the direct contact method, the results are: the AH Plus sealer showed greater antimicrobial than the Epiphany; Epiphany presented greater dissolution during all tested times (p< 0.05). A. naeslundii was the most susceptible microorganism and S. aureus the most resistant against all tested sealers. Regarding the Agar diffusion method, the greatest antimicrobial activity was achieved by the primer, followed by AH Plus and Epiphany. C. albicans was the most susceptible microorganism, while S. aureus was the most resistant. Regarding the prevention of the coronal microleakage, AH Plus/ gutta-percha presented better results than the Epiphany system (p<0.05). All teeth filled with Epiphany system presented color alteration on the root surface. Regarding the antimicrobial property of the auxiliary chemical substances on the cones, both chemical agents were unable to bind to the gutta-percha cone components and to release themselves into the Agar medium during all the periods of time tested. Nevertheless, when disinfected with 2% CHX gel, the Resilon cone demonstrated a residual action. Regarding the residual property of the disinfectants on the surface of the cones, SEM analysis showed no alteration on their superficial features. In conclusion, the results suggest that the Epiphany system was not superior to the AH Plus regarding the antimicrobial action and the prevention of the coronal microleakage, and the auxiliary chemical substances used in the disinfection of gutta-percha and Resilon cones did not show any residual action on the gutta-percha cones and did not cause any damage on the surface of both types of cones. However, the Resilon cones showed a residual antibacterial action when exposed to the chlorhexidine gel. / Doutorado / Endodontia / Doutor em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/290442 |
Date | 12 August 2018 |
Creators | Sena, Neylla Teixeira |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Gomes, Brenda Paula Figueiredo de Almeida, Schmitz, Marcia da Silva, Pinheiro, Ericka Tavares, Almeida, José Flávio Affonso de, Záia, Alexandre Augusto |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 175 p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds