rodrigues_cem_me_guara.pdf: 1067916 bytes, checksum: 304fc3131d37ab34b15724649897cab7 (MD5) / Os compósitos compreendem uma classe de material de grande importância industrial. Compósitos carbono/epóxi apresentam inúmeras vantagens em comparação aos materiais convencionais, possibilitando projetos complexos, mais leves e de elevada resistência à corrosão e à fadiga. Contudo, sua baixa resistência a carregamentos transversais requer avaliação do comportamento do material, como consequência de impacto de objetos. O foco deste trabalho foi estudar a resposta ao impacto, caracterizada como tolerância ao dano, em compósito carbono/epóxi processado via Moldagem por Transferência de Resina (RTM). Foram analisadas as propriedades do compósito carbono/epóxi obtido e a degradação de suas propriedades após impacto. Neste trabalho, foi realizada a seleção da resina epóxi e do tecido de fibra de carbono, bem como seu arranjo, a fração volumétrica e o controle dos parâmetros de injeção e de cura. A caracterização do compósito foi realizada por microscopia de inspeção acústica CScan. O estudo da tolerância ao dano foi realizado utilizando corpos de provas impactados em dois níveis de energia, conforme norma ASTM D 7136M e a sua resistência à compressão residual, conforme norma ASTM D 7137M, foi avaliada em comparação com a resistência à compressão do compósito isento de defeitos, conforme norma ASTM D6641M. Os resultados mostram redução na resistência à compressão de aproximadamente 50% e energias absorvidas a 20 J e 30 J respectivamente, de 0,51 J/cm2 e 0,58 J/cm2 para o laminado 1 e de 0,37 J/cm2 e 0,90 J/cm2 para o laminado 2 / Composites comprise a material class of high industrial importance. Carbon/epoxy composites offer a wide amount of advantages in comparison with traditional materials, enabling complex projects, lighter and with high corrosion and fatigue resistance. However, the low transverse load resistance characteristic requires an evaluation of material behavior, as a consequence of impact occurrence. The work focus was study the damage response, defined as damage tolerance, in a carbon/epoxy composite processed by Resin Transfer Moulding (RTM). It was analyzed carbon/epoxy composite properties obtained and properties degradation after impact test. In this work were done the selection of epoxy resin and reinforcement, further the lay-up of carbon fabric, volumetric fraction and injection and curing parameters control. The composite assessment was done by acoustic microscopy inspection C-Scan. The damage tolerance study was done using impacted coupons with two energy levels, in accordance to ASTM D 7136M standard, and the residual compression resistance, in accordance to ASTM D 7137M standard, was evaluated in comparison with compression resistance in a composite without damage in accordance to ASTM D 6641M standard. Results show compressive resistance reduction about 50% and absorbed energy to 20 J and 30 J respectively, of 0,51 J/cm2 and 0,58 J/cm2 for the laminate 1 and 0,37 J/cm2 and 0,90 J/cm2 for the laminate 2
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/90783 |
| Date | 24 January 2013 |
| Creators | Rodrigues, Carlos Eduardo Monteiro [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Cioffi, Maria Odila Hilário [UNESP], Paula, Alessandro Rodolfo de [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 93 f. : il. |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1, -1 |
Page generated in 0.002 seconds