Estruturação de filmes de silício amorfo hidrogenado induzida por pulsos laser de femtossegundos / Structuring hydrogenated amorphous silicon films by femtosecond laser pulses

Neste trabalho investigamos as modificações na morfologia superficial e estrutura de filmes finos de silício amorfo hidrogenado, resultantes da irradiação com pulsos ultracurtos de femtossegundos (150 fs, 775 nm e 1 kHz). Os processos de microfabricação foram conduzidos varrendo, a velocidade constante, um feixe laser com diferentes fluências (1,8 a 6,2 MJ/m2) sobre a amostra. Os espectros de transmissão apresentaram queda para amostras irradiadas, cujas imagens de microscopia eletrônica de varredura mostraram estruturas superficiais condizentes com o fenômeno de LIPSS (Laser Induced Periodic Surface Structures). Uma análise estatística das imagens de microscopia de força atômica foi realizada com um programa que identifica e caracteriza os domínios (picos) produzidos pela microfabricação. O histograma de altura da amostra irradiada com uma fluência de 3,1 MJ/m2 mostrou que a altura média dos picos produzidos é de 15 nm, menor que o centro da distribuição de alturas para uma amostra não irradiada. Porém, para fluências acima de 3,7 MJ/m2 a morfologia é dominada pela formação de agregados. Medidas de espectroscopia Raman revelaram a formação de uma fração de silício cristalino, após a irradiação com pulsos de femtossegundos, de até 77% para 6,2 MJ/m2. Determinamos ainda uma diminuição da dimensão dos nanocristais produzidos com o aumento da fluência do laser de excitação. Portanto, nossos resultados mostram que há um compromisso entre as propriedades obtidas pela microfabricação (transmissão, distribuição de picos, fração de cristalização e tamanho dos nanocristais produzidos) que deve ser levado em conta ao aplicar a técnica de microestruturação com laser de femtossegundos. / In this work we investigated surface morphology and structural modification on hydrogenated amorphous silicon (a-Si:H) thin films, resulting from femtosecond laser irradiation (150 fs, 775 nm and 1 kHz). Microfabrication processes were carried out scanning sample´s surface, at constant speed, with distinct laser fluencies (from 1.8 to 6.2 MJ/m2). A decrease was observed in the transmission spectra of irradiated samples, whose scanning electron microscopy images revealed surface structures compatible with the Laser Induced Periodic Surface Structure (LIPSS) phenomenon. A statistical analyzes of Atomic Force Microcopy images was performed using a specially developed software, that identifies and characterizes the domains (spikes) produced by the laser irradiation. The height histogram for a sample irradiated with 3.1 MJ/m2 reveals that the average height of the produced spikes is at 15 nm, which is smaller than the center of height distribution for non-irradiated sample. For fluencies higher than 3.7 MJ/m2, however, aggregation of the produced spikes dominates the sample morphology. Raman spectroscopy revealed the formation of a crystalline fraction of 77% for laser fluence irradiation of 6.2 MJ/m2, as well as a decrease in size of the produced crystals as a function of fluence. Therefore, our results indicate that there is a compromise of the sample transmission, spikes distribution, crystallization fraction and size of nanocrystals obtained by fs-laser irradiation, which has to be taken into consideration when using this material processing method.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-05052014-112028
Date20 February 2014
CreatorsGustavo Foresto Brito de Almeida
ContributorsCleber Renato Mendonça, Marcelo Nalin, Antonio Ricardo Zanatta
PublisherUniversidade de São Paulo, Física, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0014 seconds