The current study discusses the preparation and long-term performance of polymer composites used for various purposes under different ageing conditions. The first part deals with the preparation and characterization of polymer nanocomposites based on poly(ethylene-co-butyl acrylate) (EBA–13 and EBA–28 with 13 and 28 wt % butyl acrylate, respectively) and 2–12 wt % (0.5–3 vol %) of aluminum oxide nanoparticles (two types with different specific surface areas and different hydroxyl-group concentrations; uncoated and coated with, respectively, octyltriethoxysilane and aminopropyltriethoxysilane). The nanocomposite with EBA–13 showed better overall nanoparticle dispersion while EBA–28 resulted in poor dispersion, probably due to insufficiently high shear forces acting during extrusion mixing which were unable to break down nanoparticle agglomerates. The activity of hindered phenolic antioxidant (0.2 wt%) in all EBA nanocomposites was assessed by determining the oxidation induction time using DSC. The composites containing uncoated aluminium oxide nanoparticles showed a much shorter initial OIT than the pristine polymer with the same initial concentration of antioxidant, indicating adsorption of antioxidant onto the nanoparticle surfaces. Composites containing coated nanoparticles showed a significantly smaller decrease in the initial OIT, suggesting the replacement of hydroxyl groups with organic silane tails, decreasing the concentration of available adsorption sites on the nanoparticle surfaces. The decrease in OIT with increasing ageing time in dry air at 90 °C of the nanocomposites was slower than that of the unfilled pristine polymer, suggesting a slow release of antioxidant from adsorption sites. The EBA nanocomposites exposed to liquid water at 90°C showed faster decrease of OIT than samples exposed to dry or humid air. The migration rate of antioxidant was controlled by the boundary conditions in the case of ageing in humid air and liquid water. The antioxidant diffusivity was lower for the composites containing uncoated ND than for the composites containing ND coated with octyltriethoxysilane or aminopropyltriethoxysilane. The migration and chemical consumption of deltamethrin DM, (synthetic pyrethroid) and synergist piperonyl butoxide from molded polyethylene sheets was also studied. Deltamethrin and piperonyl butoxide are often used for food storage and insect control purposes. DM showed no signs of crystallization and remained in a liquid state after being cooled to room temperature. Exposure of polyethylene compound sheets to liquid water (at 80 & 95 °C), caused degradation and hydrolysis of the ester bond in the DM, present in the prepared material, and generated species containing hydroxyl groups. Liquid chromatography and infrared spectroscopy showed a significant migration of the active species in liquid water, whereas in air at 80 °C (60 and 80 %RH) the loss of DM and PBO was negligible over 30 days. The long-term performance of medium-density polyethylene stabilized with six different phenolic antioxidants (0.1 wt%) in aqueous chlorinated media at 70 °C was studied. The results were compared with data for previously studied solutions of antioxidants in squalane (a liquid, low molar mass analogue of polyethylene). A linear relationship was established between the time to reach antioxidant depletion in polyethylene tape samples and the time in squalane samples. Infrared spectroscopy and scanning electron microscopy of drawn samples revealed the onset of surface oxidation and surface embrittlement in tape samples exposed beyond the time for antioxidant depletion. / <p>QC 20121109</p> / Cable insulation materials / Loss of deltamethrin and pipronyl butoxide from polyethylene / long-term performance of polyethylene in chlorine dioxide water
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-104685 |
| Date | January 2012 |
| Creators | Nawaz, Sohail |
| Publisher | KTH, Polymera material, Stockholm |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Doctoral thesis, comprehensive summary, info:eu-repo/semantics/doctoralThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Trita-CHE-Report, 1654-1081 ; 2012:44 |
Page generated in 0.0026 seconds