Síntese de látices hibridos de poliestireno e argila montmorilonita pelos mecanismos de polimerização via radical livre em emulsão e miniemulsão / Synthesis of polystyrene and montmorillonitic clay hybrid latexes by free radical emulsion and miniemulsion polymerization.

Materiais nanocompósitos híbridos polímero-argila nos quais lamelas nanométricas de argila montmorilonita são encapsuladas e dispersas em matriz polimérica são em geral mais rígidas, tenazes e resistentes do que os materiais poliméricos convencionais e tem o potencial de aplicações em revestimentos e filmes com propriedades de barreira. Dentre as várias técnicas de preparação de nanocompósitos poliméricos, as técnicas de polimerização \"in-situ\" em emulsão e mini-emulsão vem sendo empregada na síntese de látices híbridos com lamelas de argilas encapsuladas pelo polímero. Neste trabalho foram preparados látices híbridos de poliestireno e argila montmorilonita esfoliada através de dois métodos: no primeiro, a polimerização em emulsão e miniemulsão convencional na presença de argila modificada com sal quaternário de amônio é realizada com surfatante catiônico; no segundo método, um surfatante aniônico reativo foi usado para modificar uma argila natural sódica e empregada na polimerização em emulsão. Os resultados obtidos tanto para a polimerização em emulsão como em miniemulsão empregando idênticos reagentes (argila organofílica modificada e surfatante catiônico) mostraram boa conversão, aumento na velocidade de polimerização com aumento da concentração de surfatante e de argila, aumento na temperatura de pico na máxima velocidade de decomposição (TG), aumento no módulo de armazenamento no patamar vítreo e no patamar borrachoso (DMTA) com aumento da concentração de argila, encontrando um valor mínimo em ambos a 5% de argila. Apesar dessas características positivas, não foi obtida a encapsulação das lamelas da argila que era o objetivo principal do trabalho. Por outro lado, o método de polimerização em emulsão não convencional com surfatante reativo mostrou baixa eficiência na conversão mas que se mostrou eficaz na encapsulação das lamelas da argila para os látices com baixa conversão e elevado diâmetro de partícula. / Polymer-clay nanocomposite materials, in which nanometer-thick layers of clay dispersed in polymers, are generally stiffer, stronger, and tougher than normal polymeric materials and can be potentially useful in a variety of applications. These polymer-clay nanocomposites can be prepared in several ways, namely by emulsion \"in-situ\" polymerisation where polymer chains are coagulated on silicate layers producing capped silicate layers are more or less uniformly dispersed in aqueous medium. The objective of this work is to prepare polymer-clay hybrid latexes with exfoliated clay platelets encapsulated inside latex particles in order to improve the exfoliation of the clay platelets in the final polymeric film. To achieve this objective two separate approaches have been investigated, first by conventional emulsion polymerization and miniemulsion polymerization in the presence of montmorillonite clay modified by cationic surfactant and in the other approach a reactive anionic surfactant was used to modify the natural montmorillonite clay layers by emulsion polymerization. The results for both the emulsion polymerization as in miniemulsion using identical reagents (organoclay modified and cationic surfactant) showed good conversion, polymerization rate increased with increasing concentration of surfactant and clay, increased peak temperature at maximum speed decomposition (TG), an increase in storage modulus in the glassy plateau and the rubbery plateau (DMTA) with increasing concentration of clay, finding a minimum value in both the 5% clay. Despite these positive characteristics, encapsulation was not obtained from lamellar clay that was the main objective. Moreover, the method of emulsion polymerization with non-conventional reactive surfactant showed low conversion efficiency but has proved effective in the encapsulation of the lamellae of the clay for the lattices with low conversion and high particle diameter.

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-27092012-104639
Date17 September 2010
CreatorsFatima Cristina Torres de Souza
ContributorsHugo Ricardo Zschommler Sandim, Clodoaldo Saron, Carlos Yujiro Shigue, Gilmar Patrocínio Thim
PublisherUniversidade de São Paulo, Engenharia de Materiais, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0021 seconds