This dissertation discusses results of crystallization kinetic, morphology and scattering studies on miscible semi crystalline blends of poly(pivalolactone)/ poly(vinylidene fluoride)(pPVLIPVF₂) and poly(pivalolactone)/poly(vinylidene fluoride <i>co</i>- tetrafluoroethylene)(95-5) (PPVL/P(VF2-TFE)(95-5)) prepared by solution blending. The spherulitic growth rates of the α-phase PPVL from miscible blends with PVF₂ or P(VF₂- TFE)(95-5) were measured by polarized optical microscopy as a function of blend composition and isothermal crystallization temperature, Tx, between 160°C and 215.5°C. The PPVL weight fraction in the blends ranged from 100 to 10 wt%. Using the Lauritzen-Hoffman kinetic theory of polymer crystal growth, the equilibrium melting temperatures of the α-phase PPVL in both the PPVL/PVF₂ and the PPVL/P(VF₂-TFE)(95-5) blends have been determined, for the first time, directly from the spherulitic growth rate data. Analysis of the composition dependence of the nucleation constant, Kg suggests that the α-phase PPVL crystal/melt lateral interface free energy, Ï , in the blends decreases markedly with increasing PVF₂ or P(VF₂-TFE)(95-5) concentration. / Ph. D.
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/40312 |
| Date | 10 November 2005 |
| Creators | Huang, Jiang |
| Contributors | Chemistry, Marand, Hervé L., Gibson, Harry W., Riffle, Judy S., Wightman, James P., Wilkes, Garth L. |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Language | English |
| Detected Language | English |
| Type | Dissertation, Text |
| Format | xiii, 167 leaves, BTD, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 34348067, LD5655.V856_1995.H835.pdf |
Page generated in 0.0077 seconds