Diamond cuboid-, rhombohedron- and hexagon-shaped nanocrystals as well as branched rods of the solid solution Co1-xMnxO have been synthesized via a solvothermal synthetic route from manganese formate and cobalt acetate at elevated temperature. Rhombohedra and hexagons have dimensions no larger than 50 nm on the longest axis, rods have branches up to 150 nm long and cuboids grow up to 250 nm on a side. X-ray and electron diffraction and transmission electron microscopy analyses show that these nanoparticles are single crystals of wurtzite-type and rock salt-type Co1-xMnxO. Varying the surfactant, water and precursor ratios allows control of particle size, morphology and stoichiometry. Extending growth time at high temperatures (>370°C) leads to the disappearance of the wurtzite phase due to Ostwald ripening. Longer reaction times at temperatures between 345-365°C lead to more crystalline wurtzite-lattice particles. These results show that nanoparticle morphologies and crystal lattices arise from crystal growth and Ostwald ripening at different rates selecting for either small, smooth-surfaced wurtzite lattice particles or large, dendritically-grown rock salt lattice particles.
Identifer | oai:union.ndltd.org:RICE/oai:scholarship.rice.edu:1911/71699 |
Date | 24 July 2013 |
Creators | Walsh, Sean |
Contributors | Whitmire, Kenton H. |
Source Sets | Rice University |
Language | English |
Detected Language | English |
Type | thesis, text |
Format | application/pdf |
Page generated in 0.0013 seconds