Fabricação de compósitos de matriz metálica da liga de alumínio AA1100 com reforço cerâmico de Óxido de Zinco através de técnicas de metalurgia do pó

Submitted by Fabio Sobreira Campos da Costa (fabio.sobreira@ufpe.br) on 2017-04-04T13:36:40Z
No. of bitstreams: 2
license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5)
Dissertação_Mestrado_(Andre E. Poroca Lins)_Final.pdf: 64666922 bytes, checksum: 584e69803acfdd0b31e2b58094eb9b6c (MD5) / Made available in DSpace on 2017-04-04T13:36:40Z (GMT). No. of bitstreams: 2
license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5)
Dissertação_Mestrado_(Andre E. Poroca Lins)_Final.pdf: 64666922 bytes, checksum: 584e69803acfdd0b31e2b58094eb9b6c (MD5)
Previous issue date: 2015-01-28 / Os materiais com óxido de zinco vêm passando por um rápido desenvolvimento
devido as suas potenciais aplicações em uma ampla variedade de áreas
tecnológicas, tais como eletrônica, catálise, cerâmica, fotodetectores, sensores,
células solares, entre outras. Porém, torna-se fundamental o estudo das
propriedades, condições de síntese e aplicações. Um material que vem se
destacando devido as suas propriedades mecânicas, elétricas, magnéticas, ópticas
e químicas é o óxido de zinco (ZnO). No óxido de zinco tais propriedades dependem
principalmente do tamanho e morfologia de suas partículas. O avanço no
desenvolvimento de materiais com óxido de zinco vem recebendo bastante destaque
no meio científico e se tornando de fundamental importância devido à
interdisciplinaridade entre vários campos da ciência, e por permitir a obtenção de
novos materiais com melhores propriedades físicas e químicas. O objetivo principal
desse trabalho é produzir um compósito de matriz de alumínio AA1100, reforçado
com material cerâmico, o óxido de zinco (ZnO), utilizando o processo de metalurgia
do pó e técnica de moagem de alta energia. Para tanto, utilizou-se a caracterização
por microscopia ótica (MO), microscopia eletrônica de varredura (MEV), difração de
raios X (DRX) e difração a laser para avaliar as características do compósito, além
de verificar as propriedades mecânicas inerentes e constatar a superioridade em
relação a materiais produzidos de forma convencional. No primeiro momento é feita
a avaliação da mistura dos pós produzidos, segundo variação percentual do reforço
e tempo de processamento, com o objetivo de obter dados iniciais. Em seguida, é
feito o processamento das misturas dos pós para compactação e sinterização;
visando obter pastilhas do compósito, nas quais serão feitas ensaios e
caracterização microestrutural, e por fim avaliação de resultados e conclusões. / The zinc oxide composites materials are undergoing rapid development due to their
potential applications in a wide variety of technological areas such as electronics,
catalysis, ceramics, photodetectors, sensors, solar cells, among others. However, it
is fundamental the studies of the properties, synthesis conditions and applications. A
material that has been highlighted due to its mechanical, electrical, magnetic, optical
and chemical properties is the zinc oxide (ZnO). In zinc oxide such properties mainly
depend on the size and morphology of the particles. The technological progress in
the development of materials with zinc oxide has been receiving a lot of attention in
the scientific community and becoming of paramount importance due to several
interdisciplinary fields of science, and for allowing the obtaining of new materials with
improved physical and chemical properties. The main objective of this work is to
produce matrix composites of aluminum alloy AA1100, reinforced with ceramic
material, the zinc oxide (ZnO), the process of using powder metallurgy technique and
high energy milling. For this we used the characterization by optical microscopy
(OM), scanning electron microscopy (SEM), X-ray diffraction (XRD, and laser
diffraction to evaluate and compare the features of composite, besides checking the
mechanical properties and see the inherent superiority over conventionally produced
material. At first assessment is made of the mixture of powders produced according
to percentage change in the reinforcement and processing time, in order to obtain
initial data. Then the processing is done mixtures of powders for compaction and
sintering, to obtain tablets composite in which are made tests and microstructural
characterization, and ultimately evaluating the results and conclusions.

Identiferoai:union.ndltd.org:IBICT/oai:repositorio.ufpe.br:123456789/18476
Date28 January 2015
CreatorsLINS, André Emanoel Poroca
Contributorshttp://lattes.cnpq.br/6740759499723367, ARAÛJO FILHO, Oscar Olímpio de
PublisherUniversidade Federal de Pernasmbuco, Programa de Pos Graduacao em Engenharia Mecanica, UFPE, Brasil
Source SetsIBICT Brazilian ETDs
LanguageBreton
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Repositório Institucional da UFPE, instname:Universidade Federal de Pernambuco, instacron:UFPE
RightsAttribution-NonCommercial-NoDerivs 3.0 Brazil, http://creativecommons.org/licenses/by-nc-nd/3.0/br/, info:eu-repo/semantics/openAccess

Page generated in 0.0022 seconds