Applications of Zinc Oxide Nanotip Prepared by Aqueous Solution Deposition on Photonic Devices

In this study, we prepare the zinc oxide nanotip with aqueous solution deposited on ZnO nucleation layer. The thermal annealing with N2 ambiance at 300 oC for 1 hr increase the UV emission and decrease the defects. We use ZnO nanotip as an anti-reflection layer because of surface roughness and optical interference. ZnO nanotip with rough surface decreases reflection, so we use ZnO nanotip as an anti-reflection layer, after grown ZnO nanotip on solar cell the efficiency of solar cell was enhancement.
The coordination modes were measured by Fourier-transform infrared spectrometer (FTIR). The physical properties were characterized by X-ray diffraction (XRD). The optical properties were measured by Micro-photoluminescence (Micro-PL). The morphology was observed by field emission scanning electron microscope (FE-SEM). The performance of the cells was measured by a semiconductor device analyzer. In our results, we grow the high performance of ZnO nanotip on solar cell to increase the efficiency. The short-circuit current increased from 42 to 51 mA, and the efficiency increased from 15.7 to 18.8 %.

Identiferoai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0725112-152843
Date25 July 2012
CreatorsChien, Yu-kai
ContributorsTsu-hsin Chang, Jeng Gong, Ming-kwei Lee, Chen-lin Ho
PublisherNSYSU
Source SetsNSYSU Electronic Thesis and Dissertation Archive
LanguageEnglish
Detected LanguageEnglish
Typetext
Formatapplication/pdf
Sourcehttp://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0725112-152843
Rightsuser_define, Copyright information available at source archive

Page generated in 0.0018 seconds