This thesis deals with the study of GaAs surface properties and with methodology of metal (mainly gold) nanoparticles deposition on GaAs substrate. GaAs has complicated surface oxides structure, which are very reactive when exposed to various chemicals (both acids and alkalines) and therefore they change GaAs surface properties. That is why the study of this properties is crucial for understanding of GaAs surface reactions on metal particles colloidal solution, from which the nanoparticles are deposited on the surface. The possibilites of GaAs surface etching and passivation are discussed. These should lead to surface stability enhancement during colloidal nanoparticles deposition. There was also studied the influence of adhesive polymer monolayer grown on GaAs substrate to the amount of nanoparticles deposited to the surface after substrate immersion into colloidal solution. This thesis concentrates on analyzing of methods, how the gold colloidal nanoparticles can be deposited selectivelly, only to defined areas. The areas were defined using charged particle beam.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:383529 |
| Date | January 2018 |
| Creators | Rudolfová, Zdena |
| Contributors | Mikulík, Petr, Horová, Ivana, Kolíbal, Miroslav |
| Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0025 seconds