Title: Local structure of hexagonal ferrites studied by NMR Author: Karel Kouřil Department/Institute: Department of Low Temperature Physics Supervisor of the doctoral thesis: prof. RNDr. Helena Štěpánková, CSc. Abstract: Hexagonal ferrites of M, W, X and Y structure types were studied by means of NMR, electronic structure calculations and magnetoelectric experi- ments. Presented results deal with cation distribution, localization of ferrous ions, interpretation of NMR spectra of studied materials and effects of size reduction. In oriented layers M type strontium ferrite and submicron particles of M type barium ferrite pronounced effects of reduced size were observed on 57 Fe NMR spectra. Performance of magnetoelectric barium-strontium Y type hexaferrites with divalent zinc cations improved upon thermal treatment of samples while distribution of zinc was not significantly altered. In Sc sub- stituted BaM, Sc content was found to be uniform throughout TSSG grown crystal. In LaSrM systems electron localization in 2a sublattice was observed, co-substitution with La+Zn, La+Co and La+Cu was found to lead to partial charge compensation. In strontium ferrites of type W and X localization of ferrous ions in octahedral sites in SS block pair was observed. Keywords: NMR, hexagonal ferrites, structure,...
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:329259 |
| Date | January 2013 |
| Creators | Kouřil, Karel |
| Contributors | Štěpánková, Helena, Pištora, Jaromír, Schneeweiss, Oldřich |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/doctoralThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0024 seconds