Indiana University-Purdue University Indianapolis (IUPUI) / This study represents a cost-effective method to advance the physical and mechanical properties of carbon fiber-reinforced polymer (CFRP) prepreg composite materials,
where electrospun multiwalled carbon nanotubes (CNTs)/epoxy nanofibers fabricated and deposited in between the layers of traditional CFRP prepreg composite. CNT-aligned epoxy nanofibers were uniformly formed by an optimized electrospinning method. Electrospinning is considered one of the most flexible, low-cost, and globally recognized methods for generating continuous filaments from submicron to tens of nanometer diameter. Nanofilaments were incorporated precisely on the layers of prepreg to accomplish increased adhesion and interfacial bonding, leading to increased strength and enhancements in more mechanical properties. As a result, the modulus of the epoxy and CNT/epoxy nanofibers were revealed to be 3.24 GPa and 4.84 GPa, leading to 49% enhancement. Furthermore, interlaminar shear strength (ILSS) and fatigue performance at high-stress regimes improved by 29% and 27%, respectively. Barely visible impact damage (BVID) energy improved considerably by up to 45%. The thermal and electrical conductivities were also increased considerably because of the highly conductive CNT networks present in between the CFRP layers. The newly introduced approach was able to deposit high content uniform CNTs at the ply interface of prepregs to enhance the CFRP properties, that has not been achieved in the past because of the randomly oriented high viscosity CNTs in epoxy resins.
| Identifer | oai:union.ndltd.org:IUPUI/oai:scholarworks.iupui.edu:1805/25960 |
| Date | 05 1900 |
| Creators | Wable, Vidya Balu |
| Contributors | Dalir, Hamid, Agarwal, Mangilal, Tovar, Andres |
| Source Sets | Indiana University-Purdue University Indianapolis |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Rights | Attribution 4.0 International, http://creativecommons.org/licenses/by/4.0/ |
Page generated in 0.0018 seconds