O presente trabalho descreve a síntese de nanopartículas de prata estabilizadas em poliacrilamida (AgNP/PAM) e em polivinilpirrolidona (AgNP/PVP) por química assistida via micro-ondas, bem como a síntese de nanotubos de titânio (TiO2NT) através do mesmo método. As estruturas formadas foram caracterizadas por espectroscopia difusa no ultravioleta visível (DRS UV-Vis Vis – UV-Vis Diffuse Reflectance Spectroscopy), isotermas de adsorção/dessorção de nitrogênio, microscopia eletrônica de transmissão (MET) e de varredura (MEV), espectroscopia por energia dispersiva de raio-X (EDS – Energy Dispersive X-ray Spectroscopy), análise termo-gravimétrica (TGA – thermogravimetric analysis), difração de raios-X (DRX), espectroscopia de absorção no infravermelho (FTIR – Fourier Transform Infrared Spectroscopy) e espectroscopia de fotoelétrons de raios-X (XPS – X-Ray Photoelectron Spectroscopy). A formação de partículas com pequenos diâmetros foi obtida em ambos os sistemas de estabilização (distribuição bimodal com NPs maiores de 1,83 nm para PAM e uma distribuição multimodal para o PVP com diâmetros de 0,91 a 11,93 nm). Os espectros de XPS mostram a presença de prata elementar, bem como dos polímeros de estabilização. Para os TiO2NT, o diâmetro interno médio obtido foi cerca de 3,72 nm com espessura de parede de ~4,75 nm, com comprimentos bem variados. As nanoestruturas sintetizadas (TiO2NT e AgNP) foram combinadas para preparar fotocatalisadores e testes de degradação de um corante, alaranjado de metila, foram realizados, mostrando uma atividade maior dos TiO2NT quando em presença de AgNPs. Testes de atividade bacteriológica foram realizados com as AgNPs sintetizadas. Tanto as AgNP/PAM quanto as AgNP/PVP apresentam 100% de inibição de crescimento de colônias de Staphilococcus aureus e Escherichia coli resistentes à ampiciliana e >95% de inibição de crescimento de colônias de Escherichia coli, quando em concentrações de 1,25 ppm. As AgNPs também foram enxertadas em filmes de polissulfona (PSU) previamente tratados com radiação UV em presença de oxigênio e suas propriedades bactericidas foram estudadas. Nestes, não houve resultados conclusivos contra S. aureus, já contra E. coli houve uma inibição de crescimento de cerca de 83% para PSU/AgNP(PAM) e 67% para PSU/AgNP(PVP). O mesmo comportamento é observado contra as bactérias resistentes à ampicilina, havendo inibição de cerca de 74% PSU/AgNP(PAM) e 57% para PSU/AgNP(PVP). / The present work describes the synthesis of silver nanoparticles (NPs) stabilized with polyacrylamide (AgNP/PAM) and polyvinylpyrrolidone (AgNP/PVP) by microwave assisted chemistry, as well as the synthesis of titanium nanotubes (TiO2NT) by the same method. The formed structures were characterized by UV-Vis Diffuse Reflectance Spectroscopy (DRS UV-Vis), nitrogen adsorption/desorption isotherms, transmission (TEM) and scanning electron microscopies (SEM), X-ray energy dispersive spectroscopy (EDS), thermogravimetric analysis (TGA), X- ray diffraction (XRD), infrared absorption (FTIR) and photoelectron X-ray spectroscopy (XPS). Synthesized NPs showed small diameters in both methods (about 1.83 nm to PAM and a multimodal distribution for the PVP 0.91 – 11,93 nm). XPS spectra show the presence of elementary silver and the stabilization polymers. For TiO2NT, the internal average diameter obtained was about 3,72 nm with a wall thickness of ~ 4.75 nm and different lengths. AgNPs and TiO2NT were combined to prepare new photocatalysts for testing their dye photodegradation properties. The new photocatalysts showed higher activity than without the presence of AgNPs. The prepared AgNPs were tested to know their anti-bacteriological activities. AgNP/PAM and AgNP/PVP showed 100 % inhibition of colony growth of Staphylococcus aureus and ampicillin resistant Escherichia coli, and an inhibition of colony growth > 95 % of Escherichia coli, when the concentration was 1.25 ppm. Additionally, AgNPs grafted on the functionalized surface of polyssulfone (PSU) films. No conclusive results were obtained for S. aureus. On the contrary, in the case of E. coli there was an inhibition of growth of about 83 % for PSU/AgNP (PAM) and 67% for PSU/AgNP (PVP). The same behavior was observed with ampicillin-resistant bacteria, with inhibition of about 74% for PSU / AgNP (PAM) and 57% to PSU / AgNP (PVP).
Identifer | oai:union.ndltd.org:IBICT/oai:lume.ufrgs.br:10183/106939 |
Date | January 2014 |
Creators | Scheffer, Francine Ramos |
Contributors | Weibel, Daniel Eduardo |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UFRGS, instname:Universidade Federal do Rio Grande do Sul, instacron:UFRGS |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0242 seconds