Orientadores: Nelson Eduardo Duran Caballero, Silvia Stanisçuaski Guterres / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-14T14:13:53Z (GMT). No. of bitstreams: 1
Camargo_ZaineTeixeira_D.pdf: 3911237 bytes, checksum: 891d323a5b01460e5b5c5e924fab41ac (MD5)
Previous issue date: 2009 / Resumo: Nesse trabalho, foram preparadas nanocápsulas (NC) que consistem em um núcleo oleoso (sistema reservatório) e uma parede polimérica, nas quais se empregou o óleo palmitato de retinila (PR) e o polímero biodegradável poli(D,L-lactídeo) (PLA). Além desse sistema, nanoemulsões (NE, sem a parede polimérica) e nanoesferas (NS, matriz polimérica) foram preparadas para efeito de comparação. Utilizou-se ainda, moléculas modelos solubilizadas no núcleo oleoso do PR, a benzofenona-3 (BZ3) e a baicaleína (BAI). As NC foram caracterizadas quanto à eficiência de encapsulamento, estabilidade física e química, distribuição de tamanhos e potencial zeta. As NC e NE apresentaram tamanhos médios de 200 nm (P.D.I=0,1), potencial zeta de aproximadamente -10 mV (emprego de surfactante não-iônico), sendo estáveis físico-quimicamente por 4 meses a aproximadamente 4 °C e 28 °C. Realizou-se ensaios de citotoxicidade e fototoxicidade das nanoestruturas em queratinócitos (HaCat) e fibroblastos (BALB/c 3T3), observando-se que as NC apresentam citotoxicidade apenas a elevadas concentrações, sendo assim, apresentam-se viáveis para aplicação dérmica. Medidas de calorimetria diferencial de varredura (DSC) evidenciaram que as nanoestruturas apresentam abaixamento de picos de fusão em comparação às misturas físicas e que devido à baixa proporção, a BZ3 não influencia os eventos térmicos das nanoestruturas, enquanto que o surfactante Span 60 aumenta a largura do pico de fusão do PR, o que sugere sua solubilização no núcleo das NC. A análise morfológica das partículas pela técnica de microscopia eletrônica de transmissão (TEM) mostrou que as NC apresentam capacidade de deformação. Para melhor investigação desta propriedade, utilizou-se experimento de extrusão em membranas de poros de menores tamanhos. No ensaio, observou-se que as NC permeiam as membranas de policarbonato quando adicionado PEG-8L, um surfactante empregado para aumentar a permeação de lipossomas elásticos devido ao aumento da molhabilidade dos poros da membrana. Preparou-se o derivativo polimérico com o cromóforo azul do Nilo (AN) através da formação de ligação covalente dos ácidos carboxílicos terminais e amina do AN. Tal polímero foi empregado em ensaio de permeação cutânea por célula de difusão vertical de Franz e sua avaliação por microscopia de varredura a laser confocal (CLSM). Os ensaios revelaram que a fluorescência da parede polimérica e a do PR apresentam-se em mesma profundidade na pele, o que evidencia a permeação do carreador ao invés de uma liberação do ativo. Em quantificação das NC na pele, observou-se que, o PR atinge a célula receptora e é encontrado em camadas da epiderme/derme e camada córnea. Desta forma, esse trabalho contribuiu através da obtenção de um sistema de NC bastante promissor para o armazenamento da vitamina A, bem como no carreamento de bioativos a camadas mais profundas da pele. / Abstract: In this work, we have prepared nanocapsules (NC) that are drug-reservoir vesicular systems, in which the shell is polymeric. Retinyl palmitate (RP) was encapsulated for the first time as an oil core with poly(D,L-lactide) (PLA) shell. Nanospheres (NS, without oil core), nanoemulsions (NE, without polymer shell) and niosomes (NI, without oil and polymer) were prepared for comparison. Further, NC were used to encapsulate two model molecules, benzophenone-3 (BZ3) and baicalein (BAI). These systems were characterized and tested by a range of techniques, including encapsulation efficiency and stability by HPLC dosage, pH, size distribution and zeta potential measurements. Dynamic Light Scattering (DLS) measurements on the nanocapsules showed a monomodal peak at 200 nm (polydispersity = 0.10). The zeta potential was -10 mV (by using non-ionic surfactant). The NC system was stable for at least 4 months around 4 °C and 28 °C . Cytotoxicity and phototoxicity assays were performed in keratinocytes (HaCat) and fibroblasts (BALB/c 3T3), showing that the NC are cytotoxic only at high concentrations. Differential scanning calorimetry (DSC) showed a decrease in the fusion temperatures of the nanostructures in comparison to mixed raw materials. BZ3 incorporation did not change thermal events, and also larger fusion peak of RP was observed by incorporating liposoluble surfactant Span 60. In addition, TEM images suggested that the PLA nanocapsules display some elastic characteristic. For a better investigation, permeation through 50 nm pores of two crossed membranes at transepidermal pressure were evaluated and showed that NC are able to cross the membranes when PEG-8L is used, which is a surfactant commonly used in order to increase the pore wettability in assays with elastic liposomes. The PLA were additionally functionalized with Nile blue dye (NB) by a covalent bond formation. This PLA-NB labeled material was used in the nanostructures preparations before permeation studies by Franz diffusion cells. Both fluorescence from the RP and functionalized polymer, were found in the same depth in the skin, showing that the nanocarrier is able to permeate the skin, instead of a release of the active. The quantification by HPLC showed that after 24 h permeation studies the RP is found in the receptor chamber. Overall, these novel and versatile polymeric NC show a huge potential for pharmaceutical applications due to their excellent permeation through the skin which makes this system particularly attractive for drug delivery applications, such as in transcutaneous applications. / Doutorado / Físico-Química / Doutor em Ciências
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/248940 |
| Date | 14 August 2018 |
| Creators | Camargo, Zaine Teixeira |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Guterres, Silvia Stanisçuaski, Duran Caballero, Nelson Eduardo, 1942-, Bergman, Bartira Rossi, Tedesco, Antonio Claudio, Sabadini, Edvaldo, Jorge, Renato Atilio |
| Publisher | [s.n.], Universidade Estadual de Campinas. Instituto de Química, Programa de Pós-Graduação em Ciências |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 125 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.003 seconds