Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2014. / Made available in DSpace on 2014-08-06T18:08:12Z (GMT). No. of bitstreams: 1
327115.pdf: 3760551 bytes, checksum: 98fdbbb5eb2dbee5c332992cb28bfade (MD5)
Previous issue date: 2014 / Ligantes alternativos têm sido extensivamente estudados para substituir, total ou parcialmente, o tradicional ligante de cobalto em metais duros. Entre os ligantes comumente adotados, o níquel tem recebido maior atenção devido aos seus aspectos econômicos e similares propriedades mecânicas. Neste trabalho, duas rotas de processamento foram desenvolvidas, envolvendo níquel na forma de óxido e de pó metálico. Os efeitos de adições de molibdênio, ferro e cromo no comportamento de sinterização e nas propriedades mecânicas de metais duros à base de níquel foram investigados. Os compósitos foram processados por metalurgia do pó convencional. As amostras foram sinterizadas em temperaturas de 1400 a 1500 °C. Os sinterizados foram caracterizados microestruturalmente e tiveram seus valores de dureza Vickers e tenacidade à fratura determinados. A composição WC-10Ni desenvolvida apresentou valores de propriedades mecânicas compatíveis com os descritos na literatura. Análises dilatométricas revelaram pequena influência do molibdênio no comportamento de sinterização do metal duro à base de níquel. A adição de ferro e cromo mostrou um deslocamento significativo do início da retração para maiores temperaturas, reduzindo a contribuição da sinterização no estado sólido para a retração total da amostra. A adição combinada de molibdênio, ferro e cromo, também deslocou significantemente o início da retração para temperaturas maiores e indicou maior inibição do crescimento de grão. A presença de carbono em excesso nas composições apresentou forte influência no aumento da densificação. O molibdênio promoveu endurecimento por solução sólida, assim como o ferro e o cromo, mas manteve valores mais elevados de tenacidade à fratura. Dentre as amostras estudadas, as composições WC-9Ni-1Mo e WC-9Ni-0,5Mo-0,5(Fe,Cr) levaram ao melhor compromisso entre o par de propriedades dureza-tenacidade à fratura. Os valores de dureza destes materiais, em torno de 1300 HV10, expressaram-se abaixo do esperado, mas com elevada tenacidade à fratura, potencializando-os para aplicações nos setores de mineração e engenharia civil.<br> / Abstract : Alternative binders have been extensively studied to replace, totally or partially, the traditional cobalt binder in cemented carbides. Among the commonly adopted binders, nickel has received the most attention due to its economic aspects and comparable mechanical properties. In this work, two processing routes have been developed, involving nickel oxide and metallic nickel powder. The effects of Mo and Fe-Cr pre-alloyed additions on sintering behavior and mechanical properties of Ni-based cemented carbides were investigated. The composites were processed by conventional powder metallurgy. The samples were sintered at temperatures ranging from 1400 to 1500 °C. Sintered compacts were characterized microstructurally and had their Vickers hardness and fracture toughness determined. The WC-10Ni composition presented values of mechanical properties compatible with those described in literature. Dilatometric analyses revealed little influence of molybdenum on the sintering behavior of nickel-based cemented carbide. The addition of iron and chromium showed a significant shift in the onset of shrinkage for higher temperatures, decreasing the contribution of solid state sintering to the total shrinkage of the sample. The combined addition of molybdenum, iron and chromium, also significantly shifted the onset of shrinkage for higher temperatures and showed greater inhibition of grain growth. High carbon contents had a strong influence on increasing densification. Molybdenum promoted solid solution strengthening, as well as iron and chromium, but molybdenum also maintained higher values of fracture toughness. Among the samples studied, the WC-9Ni-1Mo and WC-9Ni-0,5Mo-0,5(Fe,Cr) compositions led to the better relation between hardness and toughness fracture. The hardness of these materials, around 1300 HV10, was lower than expected, but high fracture toughness was achieved, showing potential for applications in mining and civil engineering sectors.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/123375 |
| Date | January 2014 |
| Creators | Cabral, André Bittencourt |
| Contributors | Universidade Federal de Santa Catarina, Fredel, Márcio Celso, Klein, Aloisio Nelmo |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 154 p.| il., grafs., tabs. |
| Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
| Rights | info:eu-repo/semantics/openAccess |