In this study, DLC thin films were electrodeposited at low DC potential using a mixture of acetic acid and DI water with different ratio. The parameters of DLC thin film deposition include the DC potential, deposition temperature, concentration of electrolyte solution, were correlated to the growth mechanism. The amount of nitrogen incorporated into DLC thin films were varied with the deposited temperature. The characteristics of DLC films by various measurements such as : the I-t curves of DLC film growth, SEM, AFM, FTIR, XPS, Raman and N&K spectroscopy, were investigated in detail. Experimental results showed that the surface roughness decreased, and sp3/sp2+sp3 value of DLC increased with the deposition temperature and deposition time. Optical properties showed that the refractive index, optical energy gap increased with the deposition temperature. For SEM cross-section measurement, it showed that the thickness of DLC films decreased due to the erosion process. However, the N-DLC films become graphitization. According to our study, we find that the surface morphology of the N-DLC films are homogeneous and compact. However, with the increase of the deposition temperature, the ratio of sp3-C-N bonds increase and the ratio of sp2-C-C bonds decrease, and these lead to the increase of refractive index and optical energy gap.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0726111-154046 |
| Date | 26 July 2011 |
| Creators | Chiou, Yu-Ren |
| Contributors | Zing-way Pei, Herng-Yih Ueng, none, Tzyy-Sheng Horng, Bing-Huai Huang |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0726111-154046 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.0037 seconds