Polimerização aquosa do Metil Metacrilato (MMA) na presença da vermiculita modificada pela troca por Íons Cromo (III) e Cobalto (II). / Aqueous Polymerization of Methyl Methacrylate (MMA) in the presence of vermiculite modified by the exchange for Ions Chromium (III) and Cobalt (II).

Submitted by Johnny Rodrigues (johnnyrodrigues@ufcg.edu.br) on 2018-09-28T18:12:22Z
No. of bitstreams: 1
VILMA MARIA SUDÉRIO - DISSERTAÇÃO PPGEQ 1995..pdf: 12571558 bytes, checksum: 00b0d5b9a33da42cdeac794bde348de8 (MD5) / Made available in DSpace on 2018-09-28T18:12:22Z (GMT). No. of bitstreams: 1
VILMA MARIA SUDÉRIO - DISSERTAÇÃO PPGEQ 1995..pdf: 12571558 bytes, checksum: 00b0d5b9a33da42cdeac794bde348de8 (MD5)
Previous issue date: 1995-11-06 / Neste trabalho investigou-se a atividade catalítica da vermiculita natural (V-N) e trocada com cromo (III), (V-Cr) e cobalto (II), (V-Co), na reação de polimerização aquosa do metil metacrilato (MMA). utilizando bissulfito de sódio como iniciador. Foi estudada a influência de vários fatores, como: presença dos catalisadores V-N, V-Cr e V-Co. temperatura de calcinação dos catalisadores, massa dos catalisadores, tempo de polimerização, teor de cátions cromo (III) e cobalto(II) trocados, concentração de MMA e NaHSO? e temperatura de polimerização, sobre a velocidade de polimerização do MMA. A partir dos resultados obtidos foram observados os seguintes efeitos: 1) a V-N apresentou um efeito catalítico na reação, sendo que este efeito foi mais significativo quando os catalisadores V-Cr e V-Co foram utilizados, e que a V-Cr apresentou o maior efeito catalítico. A atividade catalítica cresceu, com o aumento dos teores dos cátions cromo e cobalto trocados; 2) o aumento da temperatura de calcinação de 100 até 800°C, das amostras V-Cr e V-Co, aumentaram a sua atividade catalítica. Entretanto, este aumento foi maior na temperatura de 400°C: 3) os efeitos dos outros fatores, citados no paragrafo anterior, mostraram um aumento na conversão do MMA. Porém, nos altos valores de conversão, foi observada a desativação dos sítios ativos, devido ao recobrimento das partículas dos catalisadores, pelo polímero formado; 4) o efeito catalítico das amostras estudadas é explicado com base no mecanismo em que a presença dos cátions de metais de transição na superfície da vermiculita. favorecem a dissociação do iniciador, produzindo maior quantidade de radicais de bissulfito, que em conseqüência aumentam a taxa de polimerização. / This work presents an investigation of the catalytic activity of the natural vermiculite (V-N) and that of vermiculite exchanged with chromium (III) (V-Cr) and Cobalt (II) (V-Co) for the aqueous polymerization of metil methacrylate (MMA), using sodium bissulfite as an initiator. The influence of various factors, as the presence of catalysts V-N, V-Cr e V-Co,
calcination temperature of catalysts, catalyst mass, polymerization time, amount of
exchanged chromium and cobalt cations, MMA and NaHSO? concentration and
polymerization temperature, on the rate of polymerization of MMA has been studied. Based on the results obtained the following effects have been observed: 1) the
samples of V-N, V-Cr and V-Co have shown catalytic activity on the aqueous
polymerization reaction of MMA, and V-Cr being more significant. The catalytic
activity was increased with the increase of the amounts of exchanged chromium and
cobalt cations; 2) the increase in the calcination temperature from 100 to 800°C for the
samples of V-Cr and V-Co increased their catalytic activity. However, this increase was
highest for 400°C; 3) the effect of other factors mentioned in the previous paragraph also
showed an increase in MMA conversion. However, for higher values of conversion, due
to covering of the catalyst particles by the polymer formed, deactivation of the active
sites was observed; 4) the catalytic effect of the samples studied is explained on the basis
of mechanism that the presence of transition metal cations on the vermiculite surface
favor the initiator dissociation and thereby more bissulfite radicals are produced which in
consequence increase the polymerization rate of the MMA.

Identiferoai:union.ndltd.org:IBICT/oai:localhost:riufcg/1846
Date28 September 2018
CreatorsSUDÉRIO, Vilma Maria.
ContributorsSWARNAKAR, Ramdayal., ASSUNÇÃO, Lígia Maria Campos., CARVALHO, Laura Hecker de., SILVA, Maristela Alves da.
PublisherUniversidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA QUÍMICA, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguagePortuguese
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis