Starting from a super saturated solid solution and two different conditions withβ′′ precipitates (T6) an Al-Mg-Si alloy was heat treated at 200◦C and investigated byhardness measurements. One of the T6 conditions was investigated with transmissionelectron microscopy (TEM). The phase transformation to post-β′′ was studiedwith TEM and there was found that post-β′′ phases nucleated on the β′′ particles.After longer overaging times the growths were larger. A simple model was proposed, and it suggested that the growth of post- β′′ phases was the first steps in thetransformation of β′′, and that the final result was a microstructure consisting onlyof post- β′′ particles
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:ntnu-18908 |
| Date | January 2012 |
| Creators | Granholt, Jason Daniel David A. |
| Publisher | Norges teknisk-naturvitenskapelige universitet, Institutt for fysikk, Institutt for fysikk |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Student thesis, info:eu-repo/semantics/bachelorThesis, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.2258 seconds