<p>Diamond and cubic boron nitride surfaces have extreme properties that can be exploited in novel tribological, electrochemical and electronic applications. Normally insulating diamond surfaces can exhibit high surface conductivities due to hydrogen termination and the nature of the surrounding atmosphere. Successful growth of cubic boron nitride thin films is hindered when harsh synthesis methods are used.</p><p>Three significant surface-related properties are addressed in this thesis using computational methods: (1) the structure, energy stability and reactivity of clean and differently terminated diamond surfaces, (2) the high surface conductivity of diamond, and (3) the adsorption-induced stability, reactivity and reconstruction of the cubic boron nitride (100) surface. Density Functional Theory (DFT) has been used at the GGA level under periodic boundary conditions to simulate the diamond and cubic boron nitride surfaces. </p><p>The diamond surface structures are shown to be insensitive to hydrogen desorption. Oxygen atoms bind in different positions and with different bond strengths. Hydroxyl groups experience both attractive hydrogen bonding and steric repulsions within the adsorbed species. The reconstruction of diamond (111)-1x1 is strongly dependent on the species adsorbed onto the surface. Electron transfer was observed from a diamond surface into a water-based adlayer, yielding a p-type doped surface, depending on the nature of the surface and the adlayer. The cubic boron nitride (100)-1x1 surface was shown to reconstruct into a 2x1 configuration on both the boron- and nitrogen-rich side through the formation of B-B bonds, as well as N–N dimer-induced surface relaxation. Hydrogen stabilized the (100)-1x1 surface, but the partial removal of hydrogen yielded non-reactive dimer formation on the surface. </p>
Identifer | oai:union.ndltd.org:UPSALLA/oai:DiVA.org:uu-8372 |
Date | January 2007 |
Creators | Petrini, Daniel |
Publisher | Uppsala University, Department of Materials Chemistry, Uppsala : Acta Universitatis Upsaliensis |
Source Sets | DiVA Archive at Upsalla University |
Language | English |
Detected Language | English |
Type | Doctoral thesis, comprehensive summary, text |
Relation | Digital Comprehensive Summaries of Uppsala Dissertations from the Faculty of Science and Technology, 1651-6214 ; 380 |
Page generated in 0.0011 seconds