O arame tubular AWS E71T-1 tem sido utilizado, na grande maioria das aplicaÃÃes, com CO2 e argÃnio. No entanto, para esta mistura de gÃs, as informaÃÃes nÃo foram levantadas, de forma suficiente, com relaÃÃo ao desempenho operacional do arame. Sabe-se que o tipo de gÃs afeta tambÃm a transferÃncia metÃlica, o comportamento do arco, a geometria do cordÃo de solda, a taxa de deposiÃÃo e a eficiÃncia de fusÃo do arame, dentre outras caracterÃsticas do processo de soldagem. O objetivo do trabalho consiste em realizar um levantamento das caracterÃsticas operacionais do arame tubular AWS E71T-1 empregando CO2 puro e uma mistura de CO2 + argÃnio na soldagem convencional em tensÃo constante e na soldagem com corrente pulsada. Neste sentido, foram realizadas soldas, com arame tubular AWS E71T-1 de 1,2 mm de diÃmetro, em simples deposiÃÃo, na posiÃÃo plana, em corpos de prova de aÃo ABNT 1020 com dimensÃes de 150x50x8 mm. Empregou-se uma fonte eletrÃnica de soldagem e um sistema automÃtico de posicionamento da pistola. A tensÃo de soldagem foi mantida em 23 V. A relaÃÃo entre a velocidade de alimentaÃÃo do arame e a velocidade de soldagem foi mantida entre 20 e 23, para garantir uma Ãrea adicionada aproximadamente constante de 18 mm2. analisaram-se os efeitos do tipo de gÃs de proteÃÃo (CO2 e Ar + CO2 ), da distÃncia bico de contato peÃa (20 e 25 mm), dos nÃveis de corrente (160, 180 e 200 A) e sua natureza (convencional e pulsada) sobre o comportamento do arco, sobre a geometria da solda e sobre as caracterÃsticas econÃmicas do arame (taxa de fusÃo, taxa de deposiÃÃo e eficiÃncia de deposiÃÃo). Os resultados indicam que o tipo de gÃs de proteÃÃo afeta mais significativamente a transferÃncia metÃlica e a geometria da solda, exercendo pequena influÃncia sobre as caracterÃsticas econÃmicas do arame. Constatou-se tambÃm que o efeito da intensidade de corrente sobre a operacionalidade do arame tubular AWS E71T-1 depende sensivelmente do tipo de corrente (convencional ou pulsada). / The flux cored wire AWS E71T-1 has been used in the vast majority of its applications with pure CO2 as a shielding gas. A recent study demonstrated that it is possible to improve the metallurgical characteristics of the weld metal of the flux cored wire by the application of a mixture of CO2 and argon. However, information for this gas mixture hasnât been raised sufficiently concerning the operational performance of the wire using this gas mixture. It is known that the gas type also affects the metal transfer, the behavior of arc welding, the weld bead geometry, the deposition rate and the deposition efficiency of the wire within other characteristics of the welding process. The aim of the study consists in the realization of a survey of the AWS E71T-1 flux cored wire operational characteristics (economic characteristics of the welding consumable, geometric weld characteristics, arc stability and metal transfer). Due to this, bead on plate welding was performed using the flux cored wire AWS E71T-1 with a diameter of 1,2 mm, in flat position on samples of ABNT 1020 steel with a size of 150x50x8 mm. An electronic welding source and a positioning system were used. It was sustained a welding tension of 23 V. The relationship between the wire feed speed and the travel speed was kept constant between 20 and 23 to guarantee a deposit area of approximately 18 mm2. The influence of shielding gas (CO2 and Ar and CO2 ), the contact tube-to-work (TTW) (20 and 25 mm), the welding current (160, 180 and 200 A) and its nature (conventional and pulsed) were analyzed regarding the behavior of arc welding, the weld geometry and the economic characteristics of cored wire (fusion rate, deposition rate and deposition efficiency). The results showed that the shielding gas type has more influence on metal transfer and welding geometry and little influence on economic characteristics of the cored wire. It was also shown that the effect of the current intensity on the operationally of the flux cored wire AWS E71T-1 depends perceptibly on the current type (conventional or pulsed).
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:5237 |
| Date | 16 December 2002 |
| Creators | Juscelino Chaves Sales |
| Contributors | Jesualdo Pereira Farias, HÃlio Cordeiro de Miranda, Carlos Alberto Mendes da Mota |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds