Purpose: To evaluate the in vitro shear bond strength (SBS) of orthodontic attachments using 2 self-etching primers (SEP): iBOND and G-Bond.
Methods: 180 molars were randomly divided into 12 groups. Teeth were bonded with a stainless steel button using Transbond XT composite. The bonding agents were iBOND, G-Bond, Transbond Plus SEP and Transbond XT primer (control). SBS’s immediately, 24hours and 3months were measured with their Adhesive Remnant Index (ARI).
Results: Transbond XT primer (11.22MPa) had a significantly higher immediate SBS than Transbond Plus SEP (5.32MPa), iBOND (6.69MPa) and G-Bond (8.30MPa). 24 hours, Transbond XT primer (16.65MPa) and Transbond Plus SEP (13.20MPa) had a significant increase in their SBS. No difference was observed at 3 months. ARI were significantly different between the groups at all time points.
Conclusions: iBOND and G-Bond yielded sufficient SBS’s over the three time points that may be sufficient to withstand occlusal and light archwire forces.
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:MWU.1993/4008 |
| Date | 25 June 2010 |
| Creators | Ho, Andy CS |
| Contributors | Akyalcin, Sercan (Preventive Dental Science), Swain, Vanessa (Restorative Dentistry) Wiltshire, William (Preventive Dental Science) |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | en_US |
| Detected Language | English |
Page generated in 0.0023 seconds