Opto-electronic semiconductor technology continues to grow at an accelerated pace, as the industry seeks to perfect devices such as light emitting diodes for purposes of optical processing and communication. A strive for greater efficiency with shrinking device dimensions, continually pushes the technology from both a design and materials aspect. Nanosystems such a quantum dots, also face new material engineering challenges as they enter the realm of quantum mechanics, with each system and material having markedly different electronic properties. Traditionally, the semiconductor industry has focused on materials such Group II-VI and III-V compounds as the basis material for future opto-electronic needs. Unfortunately, these material systems can be expensive and have difficulties integrating into current Si-based technology. The industry is reluctant to leave silicon due in part to silicon's high quality oxide, and the enormous amount of research invested into silicon based circuit fabrication. Although recently materials such as GaN are starting to dominate the electro-optical industry since a Si-based substitute has not been found. The purpose of the dissertation was to examine several promising systems that could be easily integrated into current Si-based technology and also be produced using simple inexpensive fabrication techniques such ion implantation. The development of optically active nano-sized precipitates in silica to form the active layer of an opto-electronic device was achieved with ion implantation and thermal annealing. Three material systems were investigated. These systems consisted of carbon, silicon and metal silicide based nanocrystals. The physical morphology and electronic properties were monitored using a variety of material characterization techniques. Rutherford backscattering/channeling were used to monitor elemental concentrations, photoluminescence was used to monitor the opto-electronic properties and transmission electron microscopy was used to study the intricate morphology of individual precipitates. The electronic properties and the morphology were studied as a function of implant dose, anneal times and anneal temperatures.
| Identifer | oai:union.ndltd.org:unt.edu/info:ark/67531/metadc5259 |
| Date | 05 1900 |
| Creators | Mitchell, Lee |
| Contributors | McDaniel, Floyd D., Holland, Orin Wayne, Duggan, Jerome L., Neogi, Arup, Littler, Chris, Weathers, Duncan L. |
| Publisher | University of North Texas |
| Source Sets | University of North Texas |
| Language | English |
| Detected Language | English |
| Type | Thesis or Dissertation |
| Format | Text |
| Rights | Public, Copyright, Mitchell, Lee, Copyright is held by the author, unless otherwise noted. All rights reserved. |
Page generated in 0.0028 seconds